Sari, Sendy Puspa Mita (2016) STUDI PEMANFAATAN LIMBAH SANDBLASTING PT X DAN LIMBAH KARBIT PT Z SEBAGAI BAHAN CAMPURAN DALAM PEMBUATAN BETON RINGAN. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.
Full text not available from this repository.Abstract
ABSTRAK Limbah sandblasting dan limbah karbit merupakan dua jenis produk sampingan yang dihasilkan oleh PT. Z dan PT. X. Berdasarkan PP No 101 Tahun 2014, limbah tersebut tergolong dalam limbah B3 dengan kategori bahaya 2. Meskipun demikian, limbah yang dihasilkan dibiarkan di ruang terbuka. Sehingga, kedua jenis limbah perlu dimanfaatkan guna memenuhi aspek K3 dan lingkungan. Tujuan penelitian ini untuk menganalisa pengaruh penambahan limbah karbit dan limbah sandblasting pada proses pembuatan beton pada kuat tekan, berat jenis, setting time, dan uji TCLP. Menganalisa pengaruh variasi komposisi pada berat jenis dan kuat tekan dengan metode statistik ANOVA. Menganalisa komposisi terbaik untuk membuat beton ringan berdasarkan uji kuat tekan, berat jenis, dan uji TCLP. Hasil penelitian menunjukkan bahwa kuat tekan beton ringan dengan penambahan limbah mengalami penurunan maupun peningkatan dari komposisi normal. Kuat tekan beton dengan penambahan limbah sandblasting sebanyak 25% dan limbah karbit sebanyak 5%, 10%, dan 15% berturut-turut sebesar 7,37 MPa (menurun 37,06%); 8,839 MPa (menurun 24,52%); dan 11,84 MPa (meningkat 13%) dengan berat jenis rata-rata telah memenuhi ketentuan beton ringan yakni 1.647,8 kg/m 3 . Berdasarkan hasil uji setting time, waktu pengerasan semen mengalami peningkatan masing-masing sebesar 57,14%; 71,43%; 85,71% dari kondisi normal. Selain itu, beton tidak mengandung kadar logam berat yang melebihi baku mutu. Melalui pengujian ANOVA dapat diketahui bahwa variasi komposisi hanya berpengaruh pada kuat tekan. Pada penelitian ini, produk beton ringan dinyatakan aman bagi lingkungan dan mampu difungsikan sebagaimana mestinya sesuai dengan mutu beton normal rendah. Komposisi terbaik pada penelitian ini adalah 25% limbah sandblasting dan 15% limbah karbit. Kata kunci : Beton ringan, Sandblasting, Karbit, TCLP, Kuat tekan, Berat jenis ABSTRACT Sandblasting and carbide sludge are two types of waste that produced by PT.X and PT.Z. Based on the attachment of PP No. 101 2014, those wastes are classified as hazardous waste. But, both of those companies didn’t do any management effort to decrease their quantity. To fulfill the safety and environmental aspect, those wastes were used as mixed material of lightweight concrete. The purpose of this study is to analyze the effect of waste addition to compressive strength, density, setting time, and the TCLP test of lightweight concrete. Analyzing the effect of composition variation to density andcompressive strength of lightweight concrete using ANOVA statistical method. Analyzing the optimum composition of sandblasting waste and carbide sludge to make a good lightweight concrete. The results showed that there’re decreasing and increasing value of compressive strength from normal composition. The compressive strength with the addition of 25% sandblasting waste and carbide sludge as much as 5%, 10%, and 15% are 7,37 MPA (decreased by 37,06%); 8,839 MPA (decreased by 24,52%); and 11,84 (increased by 13%) with an average density was 1647,8 kg/m 3 . Using wastes as mixed material, increased the setting time by 57,14%; 71,43%; 85,71% from normal condition and also the quantity of heavy metals were below the standard. The ANOVA test showed that the composition variation only affects to the compressive strengh. In this study, the lightweight concrete was safe for environment and it was able to used as it should be. The best composition was mixed of 25% sandblasting waste and 15% carbide sludge. Keyword : lightweight concrete, sandblasting, carbide, TCLP, compressive strength, density
| Item Type: | Thesis (Diploma) |
|---|---|
| Subjects: | T Technology > T Technology (General) |
| Divisions: | ?? tkdkk ?? |
| Depositing User: | Unnamed user with email repository@ppns.ac.id |
| Date Deposited: | 13 Sep 2018 03:51 |
| Last Modified: | 13 Sep 2018 03:51 |
| URI: | http://repository.ppns.ac.id/id/eprint/605 |
Actions (login required)
 |
View Item |