ANALISA DAYA REKAT CAT PADA PROSES PAINTING DENGAN VARIASI JUMLAH LAPISAN, SURFACE PREPARATION DAN APLIKATOR PADA BAJA A 36 MENGGUNAKAN METODE DESAIN FAKTORIAL

Yusufi, Akhmad Faiq (2016) ANALISA DAYA REKAT CAT PADA PROSES PAINTING DENGAN VARIASI JUMLAH LAPISAN, SURFACE PREPARATION DAN APLIKATOR PADA BAJA A 36 MENGGUNAKAN METODE DESAIN FAKTORIAL. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK PT. Bangun Sarana Baja adalah salah satu perusahan kontraktor dan fabrikasi di Indonesia yang memproduksi berbagai macam kebutuhan akan komponen-komponen kontruksi. PT. Bangun Sarana Baja menggunakan proses finishing material dengan menggunakan proses painting sebagai pencegah timbulnya korosi pada material. Penelitian ini ditujukan untuk mengetahui analisa variasi jumlah lapisan, surface preparation, dan aplikator terhadap daya rekat cat dan mengetahui nilai serta model matematik yang dapat menghasilkan daya rekat cat yang optimum pada pelat baja A 36 pada proses painting. Penelitian ini menggunakan desain eksperimen dengan menggunakan metode desain faktorial, dengan 3 faktor, 2 faktor mempunyai 2 level dan 1 faktor mempunyai 3 level berdasarkan rancangan desain faktorialdilakukan 12 kali percobaan. Kemudian dilakukan uji daya rekat cat, pengujian tersebut menggunakan pull off test, x cut dan cross cut. Penelitian ini bertujuan untuk mengetahui pengaruh jumlah lapisan, surface preparation, dan aplikator yang sesuai agar memperoleh daya rekatcat yang sesuai dengan spesifikasi perusahaan dan mengetahui optimasi proses painting untuk daya rekat cat benda uji dengan menggabungkan variasi parameter yang di ujikan. Hasil analisa pada pengujian pull off test menunjukan bahwa parameter aplikator sebagai parameter yang memiliki pengaruh signifikan dan conventional sebagai parameter optimal terhadap daya rekat cat. Pada pengujian x cut menunjukan bahwa parameter surface preparation dan aplikator sebagai parameter yang memiliki pengaruh signifikan, blasting dan conventional sebagai parameter optimal terhadap daya rekat cat. Pada pengujian cross cut menunjukan bahwa parameter jumlah lapisan dan surface preparation sebagai parameter yang memiliki pengaruh signifikan, 2 lapisandan airless sebagai parameter optimal terhadap daya rekat cat. Kata kunci : daya rekat cat, metode desain faktorial, painting ABSTRACT PT. Bangun Sarana Baja is one of the contractors and fabrication company in Indonesia which produce construction components. PT. Bangun Sarana Baja using the finishing process of material using painting process as a deterrent to corrosion of the material. This study aimed to determine the analysis of variations in the number of layers, surface preparation, and applicators to adhesion strength and know the value that can produce the optimum of adhesion strength on steel plate A 36 in painting process. This research using design of experiment using factorial design, with three factors, two factors have two levels and one factor has three levels based on the design of factorial design trial was conducted 12 times. Then the adhesion strength test, such testing using pull off test, x cut and cross cut. This study aims to determine the effect of the number of layers, surface preparation, and applicators to obtain the adhesion strength according to the company's specifications and determine the optimization of painting process for adhesion strength object by combining variations of parameters. An analysis of the pull off test showed that the parameters of the applicator as a parameter that has a significant influence and conventional as the optimal parameters of adhesion strength. On x cut testing showed that the parameters of the surface preparation and applicators has a significant influence, conventional and blasting as the optimal parameters of the adhesion strength. On cross cut testing showed that the parameters of the number of layers and surface preparation as a parameter that has a significant influence, two layers and airless as the optimal parameters of the adhesion strength. Keywords: adhesion strength, factorial design method, painting

Item Type:	Thesis (Diploma)
Subjects:	T Technology > T Technology (General)
Divisions:	?? tddm ??
Depositing User:	Unnamed user with email repository@ppns.ac.id
Date Deposited:	12 Sep 2018 06:39
Last Modified:	12 Sep 2018 06:39
URI:	http://repository.ppns.ac.id/id/eprint/567

Actions (login required)

View Item