Annadzif, Moh Khafidz (2017) ANALISA JUMLAH LAPISAN BUILD UP TERHADAP SIFAT MEKANIK, STRUKTUR MIKRO DAN LAJU KOROSI PADA MATERIAL SA-240 TP304. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.
Full text not available from this repository.Abstract
ABSTRAK Pada proses fabrikasi sering terjadi kesalahan apabila kurang teliti saat pengukuran dimensi, hal tersebut mengakibatkan proses fabrikasi membenahi kembali dengan proses build up, proses build up dilakukan dengan pengelasan pada salah satu sisi material hingga dimensi yang dibutuhkan sesuai, dengan adanya pembenahan tersebut mengakibatkan masukan panas yang besar sehingga memungkinkan sifat mekanik dari material tersebut mengalami perubahan. Dengan penambahan build up 1 lapis, 2 lapis dan 3 lapis akan berpengaruh pada hasil kekuatan mekanik dilakukan uji tarik, tekuk dan kekerasan. Untuk mengetahui ketahanan korosinya dilakukan uji korosi sel tiga elektroda. Dan untuk mengetahui struktur mikro dilakukan uji metalograpy. Dari hasil uji tarik dan tekuk proses build up 1 lapis, 2 lapis dan 3 lapis tidak mempengaruhi terhadap sifat mekaniknya. Hasil uji kekerasan di dapatkan bahwa dengan build up 3 lapis nilai kekerasannya bertambah di karenakan dengan masukan panas berulang kali mengakibatkan kandungan ferrite pada material stainless steel bertambah sehingga nilai kekerasan naik, dan pada pengujian mikro didapatkan bahwa kandungan ferite pada build up 3 lapis lebih banyak dari pada build up 1 lapis, 2 lapis dan tanpa build up. Dan dari hasil uji korosi diperoleh bahwa dengan penambahan build up 3 lapis maka laju korosinya semakin cepat di bandingkan proses build up 1 lapis, 2 lapis dan tanpa build up. Kata kunci : Build up, Sifat Mekanik, Struktur Mikro, dan Laju Korosi ABSTRACT In the fabrication process is often an error if less careful when measuring the dimensions, it resulted in the fabrication process to fix back with the build -up process, the build-up process is done by welding on one side of the material to the required dimensions accordingly, in the event of such improvements lead to a hot input So as to allow the mechanical properties of the material to undergo a change. With the addition of 1 layer build up, 2 layers and 3 layers will affect the result of mechanical strength is done tensile, buckling and hardness test. To determine its corrosion resistance is done by three cell electrode corrosion test. And to know the microstructure done by metalograpy test. From result of tensile test and buckling process of build up 1 layer, 2 layer and 3 layer not influence to its mechanical properties. The result of hardness test was found that with build up 3 layers the hardness value increased in because with the heat input repeatedly resulted the ferrite content on stainless steel material increased so that the value of hardness rose, and in micro test found that the ferite content in build up 3 layers more than On build up 1 layer, 2 layers and without build up. And from the corrosion test results obtained that with the addition of build up 3 layers then the corrosion rate faster in compare the process of build up 1 layer, 2 layers and without build up. Keywords: Build up, Mechanical Properties, Micro Structure, and Corrosion Rate
| Item Type: | Thesis (Diploma) |
|---|---|
| Subjects: | T Technology > T Technology (General) |
| Divisions: | Jurusan Teknik Bangunan Kapal > D4 Teknik Pengelasan |
| Depositing User: | Unnamed user with email repository@ppns.ac.id |
| Date Deposited: | 05 Oct 2018 05:22 |
| Last Modified: | 05 Oct 2018 05:22 |
| URI: | http://repository.ppns.ac.id/id/eprint/1327 |
Actions (login required)
 |
View Item |