Analisa Pengaruh Multiple Repair Welding Pada Water Necker Pump Menggunakan Material Pipa Cu-Ni (Copper-Nickel) Terhadap Sifat Mekanik Dan Struktur Mikro

Alifudin, Ahmad Bahrul (2017) Analisa Pengaruh Multiple Repair Welding Pada Water Necker Pump Menggunakan Material Pipa Cu-Ni (Copper-Nickel) Terhadap Sifat Mekanik Dan Struktur Mikro. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Proses pengelasan selalu ada resiko gagal dalam proses pengerjaannya maka diperlukan perbaikan atau repair, apabila kegagalan dilakukan berulang kali maka perlu dilakukan metode multiple repair welding. Multiple repair welding yang dilakukan membuat material terkena panas yang berulang-ulang dan akan menyebabkan terjadinya deformasi, perubahan metalurgi, tegangan thermal, dan perubahan struktur. Akibat terjadinya perubahan struktur maka sifat mekaniknya akan berubah. Pada penelitian tugas akhir ini menggunakan 3 variasi repair yang berbeda yaitu pengelasan yang tanpa di repair, pengelasan yang di repair 1 kali, dan pengelasan yang di repair 2 kali. Pada proses pengelasan menggunakan pengelasan GTAW. Proses pengelasan ini dilakukan dengan beberapa prosedur pengelasan dan pengujian. Untuk material yang digunakan menggunakan material pipa Cu-Ni C70600. Setelah proses pengelasan selesai dilakukan beberapa pengujian yaitu struktur mikro, uji tarik, dan uji lengkung Proses penelitian ini diketahui hasil struktur mikro terlihat bahwa semakin banyak proses multiple repair welding yang dilakukan, terlihat semakin banyak nikel yang terbentuk dan semakin besar pula struktur pada HAZ. Hasil uji tarik pada spesimen tanpa repair memiliki nilai kuat tarik sebesar 281.365 MPa, dibanding dengan spesimen dengan repair 1 kali dan 2 kali sebesar 286.863 MPa dan 281.713 MPa. Kata kunci: multiple repair welding, CU-Ni 70600, pengelasan GTAW ABSTRACT In welding process there always the possibility of failures, so the repair process is needed when the failure happen. But when it happen repeatedly, the multiple repair is consider to be done. Multiple repair welding makes the material affected of the heat continuously and makes the material deform, metallurgical changes, thermal stress and structure changes. On this research there will be three variations of repair which are the welding process without repair, welding process with a repair, and welding process with twice repair process. The welding process uses is Gas Tungsten Arc Welding (GTAW). There will be some procedures of welding and tests for this research. And for the material will be used is Cu-Ni C70600 pipe. After the welding process has been done, some tests will be conducts, which are micro structure test, tensile test and bending test. From the result of the tests turn out that the more the repair process, the higher nickel will be shown in micro structure test and the higher the HAZ size. Tensile test result on specimen without any repair process has tensile strength for about 281.365 MPa, comapared with the specimen with once and twice repair process, whch are 286.863 MPa and 281.713 MPa. Key Words: multiple repair welding, CU-Ni 70600, GTAW

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > D4 Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 03:27
Last Modified: 05 Oct 2018 03:27