PENGARUH TEKNIK TEMPER BEAD WELDING MENGGUNKAN METODE HALF BEAD TECHNIQUE DAN CONSISTENT LAYER TECHNIQUE PADA MATERIAL SA-537 CLASS 2 SEBAGAI ALTERNATIF PENGGANTI PWHT TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK

Alvin, Hirliando Noer (2017) PENGARUH TEKNIK TEMPER BEAD WELDING MENGGUNKAN METODE HALF BEAD TECHNIQUE DAN CONSISTENT LAYER TECHNIQUE PADA MATERIAL SA-537 CLASS 2 SEBAGAI ALTERNATIF PENGGANTI PWHT TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Untuk mengurangi nilai residual stress pada proses pengelasan biasanya dilakukan proses Post Weld Heat Treatment (PWHT). Namun proses PWHT sangat mahal. Sebagai pengganti PWHT terdapat alternatif lain yang lebih murah dan simple yaitu menggunakan proses Temper Bead Welding yang merupakan penempatan manik-manik las (bead) pada lokasi yang spesifik di dalam lasan maupun pada permukaan las yang bertujuan untuk mempengaruhi metallurgical properties dan HAZ dan deposit setiap pengelasan sebelumnya. Pada penelitian kali ini akan menggunakan teknik Temper bead welding CLT (Consistent Layer Technique) dan HBT (Half Bead Technique) sebagai alternatif pengganti PWHT pada material SA-537 class 2. Dalam pengerjaan tugas akhir ini dilakukan beberapa pengujian yaitu Tensile, Bending, Hardness, Impact Charpy V notch, Macro Etch dan Metalography . Sedangkan hasil struktur mikro pada pada pengelasan PWHT butirannya lebih besar dibandingkan CLT dan HBT, hal ini dikarenakan kandungan pearlite pada variasi CLT dan HBT lebih banyak dari pada PWHT. Dari pengujian hardness terlihat kekerasan HBT bisa menggantikan proses PWHT. Dan hasil nilai impact PWHT dan teknik temper bead welding memiliki selisih nilai impact yang berbeda Dari hasil 4 pengujian macro, micro, hardness dan impact kedua tehnik temper bead welding keduanya bisa menggantikan PWHT, tapi teknik yang disarankan adalah half bead technique karena paling mendekati PWHT. Kata Kunci: Post Weld Heat Treatment (PWHT), Temper bead Welding, Consistent Layer Technique (CLT), Half Bead Technique (HBT), SA-537 Class 2 ABSTRACT To reduce the residual stress value on welding process, usually Post Weld Heat Treatment (PWHT) is used for it. But economically PWHT process is so expensive. As a cheaper alternative, welding temperbead usually used as a replacement of PWHT process. Welding Temper bead is weld bead placement process in specific location, inside or surface, that means to change the metallurgical properties, HAZ and weld deposit for every weld bead before. On this research will be use temper bead welding technique CLT (Consistent Layer Technique) and HBT (Half Bead Technique) as an alternative replacement of PWHT process.. Those tests are tensile, bending, hardness, impact charpy v notch, macro etch and metalography. Meanwhile the results of micro structure show that the specimen with PWHT process has biger grain structure than CLT and HBT process. And from impact test turns out there were the differences of impact value between PWHT process and welding temperbead process on -20 o C. So from all of the tests result, it can conclude than both technique of welding temper bead can be an alternative replacement of PWHT. But for the highest recommended technique is half bead technique. Key Words: Post Weld Heat Treatment (PWHT), Temperbead Welding, Consistent Layer Technique (CLT), Half Bead Technique (HBT), SA-537 Class 2

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > D4 Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 04 Oct 2018 07:45
Last Modified: 04 Oct 2018 07:45
URI: http://repository.ppns.ac.id/id/eprint/1291

Actions (login required)

View Item View Item