Pratama, Riano Arsanta (2017) ANALISA KOMPOSISI GAS PELINDUNG PADA PENGELASAN GMAW DENGAN MATERIAL SA 240 TYPE 304 PLATE TERHADAP STRUKTUR MIKRO NILAI KEKERASAN DAN LAJU KOROSI. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.
Full text not available from this repository.Abstract
ABSTRAK Stainless steel merupakan salah satu material yang sangat diminati dalam dunia kontruksi. Keunggulan pipa ini yang memiliki sifat tahan korosi yang cukup baik serta proses pengelasan material ini yang relatif lebih mudah daripada jenis stainless steel lainya membuat aplikasi material ini sangat berfariatif. Austenitic stainless steel merupakan baja tahan karat dengan proses perlakuanya yang relatif lebih mudah Penggunaan shielding gas sangat diperlukan dalam pengelasan material austenitic stainless steel. Hal ini untuk mencegah kontaminasi dari unsur – unsur disekitar proses pengelasan berlangsung. Dalam penelitian ini digunakan shielding gas argon dan nitrogen sebagai terobosan baru dalam dunia pengelasan. Dari hasil pengelasan spesimen uji yang kemudian dilakukan uji untuk mengetahui efect dari penggunaan gas ini. Dari hasil pengujian kekerasan diketahui penggunaan gas nitrogen yang digunakan sebagai shielding gas dapat menambah nilai kekerasan pada logam las terutama pada daerah HAZ. Hal ini dikarenakan penggunaan gas nitrogen sebagai shielding gas membuat unsur nitrogen yang terkandung pada logam induk bertambah sehingga terbentuk unsur ferite pada hasil pengelasan. unsur nitrogen yang terkandung pada logam las terbukti dengan hasil uji chemical logam las yang mengindikasikan meningkatnya kandungan nitrogen pada logam las. Pengujian laju korosi yang digunakan untuk mengetahui ketahanan korosi material yang menghasilkan nilai laju korosi yang besar dalam penggunaan shielding gas nitrogen daripada gas argon yang umum digunakan dalam dunia pengelasan. Dari hasil pengujian dapat disimpulkan penggunaan gas nitrogen dapat menurunkan ketahanan korosi material. Kata kunci : Pengelasan GMAW, stainless steel jenis austenitic, kandungan nitrogen, imersion potensio dinamic sel 3 electrode, pengujian kekerasan dan struktur mikro. ABSTRACT Stainless steel is one of the most desirable materials in the world of construction. The advantages of this pipe that has a good corrosion-resistant properties and the welding process of this material is relatively easier than other types of stainless steel makes this material application is very fancy. The use of shielding gas is necessary in austenitic stainless steel welding materials. This is to prevent contamination of the elements around the welding process takes place. In this study used shielding gas argon and nitrogen as a new breakthrough in the welding world. From the results of the welding test specimen then tested to determine the effect of the use of this gas. From the results of hardness testing known the use of nitrogen gas used as shielding gas can add hardness value in welding metal, especially in the HAZ area. This is because the use of nitrogen gas as a shielding gas to make the nitrogen element contained in the parent metal increases so as to form ferite elements in the welding results. The nitrogen element contained in the welded metal is proved by the weld metal chemical test results indicating the increase of nitrogen content in the weld metal. The corrosion rate test is used to determine the corrosion resistance of the material that results in a large corrosion rate value in the use of nitrogen gas shielding rather than the argon gas commonly used in the welding world. From the test results can be concluded the use of nitrogen gas can reduce the corrosion resistance of the material. Keywords: GMAW welding, austenitic type stainless steel, nitrogen content, immersion potential dinamic cell 3 electrode, hardness testing and microstructure.
| Item Type: | Thesis (Diploma) |
|---|---|
| Subjects: | T Technology > T Technology (General) |
| Divisions: | Jurusan Teknik Bangunan Kapal > D4 Teknik Pengelasan |
| Depositing User: | Unnamed user with email repository@ppns.ac.id |
| Date Deposited: | 04 Oct 2018 07:25 |
| Last Modified: | 04 Oct 2018 07:25 |
| URI: | http://repository.ppns.ac.id/id/eprint/1285 |
Actions (login required)
 |
View Item |