Maharani, Alfidani Dwi (2017) PENGARUH TEMPERATUR PEMANASAN DAN HOLDING TIME PADA PROSES TEMPERING TERHADAP SIFAT MEKANIK DAN LAJU KOROSI BAJA PEGAS SUP 9 A. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.
Full text not available from this repository.Abstract
ABSTRAK Pada pembuatan pegas terdapat perlakuan panas yang dapat membentuk sifat mekanik material dari yang mudah patah maupun sangat kuat. Salah satu perlakuan panas tersebut adalah proses tempering. Dengan proses tempering maka suatu material dapat diperbaiki sifat mekaniknya. Tujuan penelitian ini adalah untuk mendapatkan sifat mekanik dan laju korosi material SUP 9A, dengan temperatur hardening 850ºC selama 30 menit dan selanjutnya pendinginan cepat (quenching) ke dalam media oli. Kemudian tempering dengan temperatur 300ºC, 400ºC,500 ºC dan 600ºC dengan holding time 30 dan 60 menit. Pengujian yang dilakukan meliputi uji kekerasan, ketangguhan, tarik dan laju korosi. Semakin tinggi temperatur tempering yang digunakan nilai kekerasan dan kekuatan tariknya menurun sedangkan nilai ketangguhan dan laju korosi semakin meningkat. Holding time 30 menit mempunyai nilai kekerasan dan nilai tarik yang lebih tinggi serta nilai laju korosi yang lebih rendah dibandingkan holding time 60 menit. Hasil variasi yang paling optimal yaitu pada temperatur tempering 500 ºC dan holding time 30 menit dengan nilai kekerasan 448,132 HVN, nilai ketangguhan 0,33 J/mm 2 , nilai kekuatan tarik 1333,754 Mpa dengan modulus resilien 17,050 Mpa dan laju korosi 1,0098 mm/yr. Kata kunci : Tempering, holding time, SUP 9A, sifat mekanik, quenching ABSTRACT In the manufacture of springs there is a heat treatment that can form the mechanical properties of the material from the easily broken or very strong. One such heat treatment is the tempering process. By tempering process then a material can be improved its mechanical properties. The purpose of this study was to obtain the mechanical properties and corrosion rate of SUP 9A material, with hardening temperature of 850ºC for 30 minutes and then quenching into the oil medium. Then tempering with temperature 300ºC, 400ºC, 500ºC and 600ºC with holding time 30 and 60 minutes. The tests include hardness, toughness, tensile and corrosion test. The higher tempering temperature used by the value of hardness and tensile strength decreased while the value of toughness and corrosion rate increased. Holding time 30 minutes has higher hardness and tensile value and lower corrosion rate than holding time 60 minutes. The most optimal variation result is tempering temperature 500 ºC and holding time 30 minutes with hardness value 448,132 HVN, value of toughness 0,33 J / mm2, value of tensile strength 1333,754 Mpa with resilient modulus 17,050 Mpa and corrosion rate 1,0098 mm/Yr. Keyword : Tempering, holding time, SUP 9A, mechanical properties, quenching
| Item Type: | Thesis (Diploma) |
|---|---|
| Subjects: | T Technology > T Technology (General) |
| Divisions: | ?? tddm ?? |
| Depositing User: | Unnamed user with email repository@ppns.ac.id |
| Date Deposited: | 03 Oct 2018 08:26 |
| Last Modified: | 03 Oct 2018 08:26 |
| URI: | http://repository.ppns.ac.id/id/eprint/1268 |
Actions (login required)
 |
View Item |