Pengaruh Temperatur Aplikasi Polyethylene BORSTAR HE-3450 Terhadap Kualitas Polyethylene Pada Coating 3LPE dengan Pengujian Tensile dan Impact

Effect Polyethylene Application Temperatur BORSTAR HE ? 3450 Toward Quality Polyethylene For Coating 3LPE With Tensile And Impact Test

Muhammad Ibnu Malik (6812040026)


Abstrak

Pengaruh Temperatur Aplikasi Polyethyelene BORSTAR HE-3450 terhadap Kualitas Polyethylene pada Coating 3LPE dengan Pengujian Tensile dan Impact Muhammad Ibnu Malik 1*, Budi Prasojo 2, Pekik Mahardhika 3 Mahasiswa, Politeknik Perkapalan Negeri Surabaya, Surabaya, Indonesia1* Dosen, Politeknik Perkapalan Negeri Surabaya, Surabaya, Indonesia 2 Dosen, Politeknik Perkapalan Negeri Surabaya, Surabaya, Indonesia 3 Email: muhammad.ibnumalik@ymail.com1*; budiprasojo1968@gmail.com2*; Pekikmahardhika02@gmail.com3*; Abstrak - Pada penelitian ini dilakukan studi tentang pengaruh temperatur aplikasi polyethylene BORSTAR HE-3450 terhadap kualitas polyethylene pada coating 3LPE dengan pengujian tensile dan impact. Penelitian ini perlu dilakukan mengingat pipa yang akan digunakan pada underground yang menggunakan coating 3LPE dituntut untuk memiliki kualitas yang baik, baik dari segi kekuatannya melindungi terhadap kontur tanah yang kasar maupun saat proses lowering dan handling, serta memiliki flexibilitas yang bagus untuk memudahkan proses aplikasi di lapangan dan dapat melindungi permukaan pipa agar tidak cepat terjadi korosi. Pada penelitian ini memfokuskan pada pengaruh temperatur aplikasi coating 3LPE terhadap kualitas polyethylene, temperatur yang optimal dari temperatur aplikasi untuk polyethylene, dan hubungan dari temperatur aplikasi dengan hasil nilai tensile dan impact test. Dari topik yang akan dibahas seperti yang dijelaskan tersebut, dilakukan pemvariasian temperatur saat proses produksi coating 3LPE dengan variasi temperatur sebesar 220 ? C, 230 ? C, dan 240 ? C. Dari hasil produksi coating yang telah dilakukan variasi temperatur tersebut, selanjutnya dilakukan pengujian tensile dan impact untuk mengetahui kualitas dari polyethylene dari setiap variasi temperatur aplikasi tersebut. Temperatur aplikasi polyethylene pada coating 3LPE berpengaruh pada kekuatan lapisan polyethylene pada coating 3LPE yang ditinjau dari hasil pengujian tensile dan impact. Temperatur aplikasi yang optimal untuk mendapatkan nilai tensile dan hasil impact yang baik adalah sebesar 230 ? C. Kenaikan temperatur aplikasi polyethylene tidak berbanding lurus dengan nilai tensile dan hasil uji impact. Kata kunci : Coating, Coating 3LPE, Polyethylene Borstar HE-3450,Tensile, Impact, Elastisitas


Abstract

Effect Polyethylene Application Temperatur BORSTAR HE ? 3450 Toward Quality Polyethylene For Coating 3LPE With Tensile And Impact Test Muhammad Ibnu Malik 1*, Budi Prasojo 2, Pekik Mahardhika 3 Student, Shipbuilding Institute Of Polytechnic Surabaya, Surabaya, Indonesia1* Supervisor, Shipbuilding Institute Of Polytechnic Surabaya, Surabaya, Indonesia 2 Supervisor, Shipbuilding Institute Of Polytechnic Surabaya, Surabaya, Indonesia 3 Email: muhammad.ibnumalik@ymail.com1*; budiprasojo1968@gmail.com2*; Pekikmahardhika02@gmail.com3*; Abstract - In the research doing study about effect polyethylene application temperature BORSTAR HE ? 3450 toward quality polyethylene for coating 3lpe with tensile and impact test. The background to do this research is pipe is apply in underground area must be have a good quality. Quality for strength to protect this pipe from extreme contour ground or to protect when lowering and handling, and then have to a good flexibility to make easy application process in field and can protect pipe surface from corrosion. The research focus in about effect polyethylene application temperature BORSTAR HE ? 3450 toward quality polyethylene, optimal temperature for application temperature polyethylene, and correlation application temperature with tensile and impact test value. Refer from this topic, will make variation on application temperature in coating 3LPE process with three variation temperature, 220 ? C, 230 ? C, and 240 ? C. From that condition will be test for product with tensile and impact test. Application temperature in process coating 3LPE make effect for strength the layer polyethylene in coating 3LPE, can see from result tensile and impact test. Optimal application temperature to get a good tensile and impact value is 230 ? C. Rise of application temperature polyethylene not equivalent with tensile and impact test value. Keywords: Coating, Coating 3LPE, Polyethylene Borstar HE-3450,Tensile, Impact, Elastisitas.


Detil Peneliti

Dosen Pembimbing 1 :Budi Prasojo
Dosen Pembimbing 2 : Pekik Mahardhika

Program Studi : D4 - TEKNIK PERPIPAAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.