ANALISA TEKNIS PENGGANTIAN MATERIAL PIPA DARI MATERIAL CARBON STEEL A53 GRADE B MENJADI MATERIAL HDPE (HIGH DENSITY POLYETHYLENE) PADA SISTEM PERPIPAAN FLUIDA FLUOSILICIC ACID (H2SIF6) DI PT. PETRO JORDAN ABADI

TECHNICAL ANALYSIS OF THE MATERIALS REPLACEMENT FROM CARBON STEEL A53 GRADE B PIPE INTO HDPE (HIGH DENSITY POLYETHYLENE) PIPE ON PIPING SYSTEM OF FLUOSILICIC ACID (H2SiF6) FLUIDS AT PT. PETRO JORDAN ABADI

Bastomi Tri Hatmojo (6811040042)


Abstrak

Material HDPE yang banyak digunakan untuk mengalirkan air ternyata dapat digunakan pula untuk mengalirkan bahan kimia. Seperti instalasi yang terdapat pada PT. Petro Jordan Abadi. Material HDPE digunakan sebagai material pengganti untuk material carbon steel A53 grade B yang digunakan untuk mengalirkan fluida asam fluosilika. Penggunaan material HDPE sebagai material pengganti terjadi pada line pompa P-2343A menuju line nomer 04200/350-FLA-D9-2033. Pada tugas akhir ini akan dibahas mengenai penggantian material dari material carbon steel A53 grade B menjadi material HDPE yang diaplikasikan pada line pompa P-2343A menuju line nomer 04200/350-FLA-D9-2033. Pembahasan secara khusus dilakukan untuk mengetahui ketahanan material HDPE terhadap fluida asam fluosilika dan penentuan letak dan jumlah support pada material pipa HDPE agar masih termasuk kriteria aman menurut ASME B31.3. Fluida yang mengalir pada line tersebut adalah asam fluosilika (H2SiF6) dengan temperatur operasi sebesar 400C dan tekanan operasinya mencapai 0,44 MPa. Dari hasil pengolahan data dan analisis data, dapat disimpulkan bahwa material HDPE mampu digunakan sebagai material pengganti material A53 grade B pada line ini berdasarkan kondisi operasi dan ketahanan terhadap fluidannya. Pipa HDPE yang digunakan adalah pipa dengan nominal diameter 14 dan SDR 17 yang mempunyai ukuran OD (Outside Diameter) 355.6 mm dan ketebalan 21.1 mm. Namun untuk instalasinya dilakukan penambahan support pada line tersebut.


Abstract

HDPE pipe that is widely used for water transfer is turns can be used to transfer a chemicals. Like the installation in PT. Petro Jordan Abadi. HDPE pipe is used as a replacement for carbon steel A53 grade B pipe that used to transfer fluosilicic acid (H2SiF6) fluids. The using of HDPE pipe as replacement materials is occur in line pump P-2343A to line number 04200/350-FLA-D9-2033. On this final project will be discussed regarding the replacement of the carbon steel A53 grade B pipe to HDPE pipe that applied for line pump P-2343A to line number 04200/350-FLA-D9-2033. The discussion is specially to know the resistance of HDPE material againt the fluosilicic acid fluid and determination of the location and the amount of the support so that is still secure according to ASME B31.3 standard. The fluids that will be transferred for this line is fluosilicic acid (H2SiF6) that the operation temperature is 40?C and the operation pressure is 0.44MPa. From the result of the tabulation data and analysis data, it can be concluded that the HDPE pipe is able of being as a relplacement carbon steel A53 grade B pipe for this line be based on operation condition and the resistance of this fluids. HDPE pipe that used is pipe with nominal diameter 14 and SDR 17. The dimension of this pipe is 355.6 mm for outside diameter (OD) and the thickness is 21.1 mm. But for the installation, the support for this line must be added.


Detil Peneliti

Dosen Pembimbing 1 :Arie Indartono
Dosen Pembimbing 2 : Dimas Endro Witjonarko

Program Studi : D4 - TEKNIK PERPIPAAN
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.