Analisa Proteksi Katodik Menggunakan Metode Anoda Tumbal Terhadap Efektifitas Proteksi Gas Tanam

ANALYSIS OF CATHODIC PROTECTION USING SACRIFICIAL ANODE METHOD TOWARD THE EFFECTIVENESS OF BURIED PROTECTION GAS PIPELINE

Bimo Kukuh Prasetyo (6810040031)


Abstrak

ABSTRAK Masalah yang sering timbul pada distribution pipeline gas sistem adalah korosi. Faktor-faktor yang mempengaruhi cepat atau lambatnya suatu proses korosi antara lain kondisi lingkungan/media, material konstruksi dan fungsi kontruksi. Untuk mencegah atau mengurangi korosi pada pipa maka dilakukan pelapisan (coating) dan pelindungan katodik (cathodic protection). Dalam tugas akhir ini, dilakukan pengukuran tingkat resistivitas tanah dan pH tanah pada kondisi actual di tujuh titik daerah Legundi-Gresik. Dalam pengukuran didapatkan nilai pH sebesar 7.36, 7.78, 7.52, 7.74, 7.98, 7.90, 7.80. Kemudian dilakukan pengujian untuk membandingan laju korosi antara spesimen yang menggunakan anoda tumbal Mn, Zn dan anoda tumbal Cr terhadap nilai pH tanah. Pengujian dilakukan selama 12 jam pada tiap-tiap anoda Mn, Zn dan Cr dengan kondisi nilai pH pada tanah. Kemudian nilai laju korosi dapat diperoleh dengan metode pengurangan berat. Hasil pengujian menunjukkan bahwa nilai pH tanah dapat mempengaruhi besarnya nilai laju korosi. Dari perbandingan anoda tumbal yang tahan terhadap korosi adalah Cr dengan laju korosi paling besar 0.056 mpy pada pH tanah 7.36 dan laju korosi paling kecil 0.011 mpy pada pH tanah 7.98. Untuk umur pengantian material dengan pelindung anoda yang paling panjang terjadi pada anoda Cr yaitu 6417.261 tahun kemudian material dengan menggunakan anoda tumbal Mn memiliki umur penggantian yang paling kecil yaitu 2223.303 tahun. Hasil itu diperoleh berdasarkan perhitungan Fundamentals of Metallic Corrosion dan API 570. Kata Kunci: proteksi katodik, standart API 570, Fundamentals of Metallic Corrosion book, pipa carbon steel API 5L Grade B


Abstract

ABSTRACT Problems often arise in the gas pipeline distribution system is corrosion. Factors affecting fast or slow corrosion process including environmental conditions / media, construction materials and construction functions. To prevent or reduce corrosion of pipes is carried coating and cathodic protection. In this thesis, carried out the measurement of soil resistivity and soil pH on the actual conditions in the area seven point Legundi-Gresik. In the measurement of pH values obtained at 7:36, 7.78, 7:52, 7.74, 7.98, 7.90, 7.80. Then testing for comparing the corrosion rate between specimens using sacrificial anode Mn, Zn and Cr to the pH value of the soil. Tests carried out for 12 hours on each anode Mn, Zn and Cr with a pH value of soil conditions. Then the value of the corrosion rate can be obtained by the method of weight reduction. The test results showed that the pH value of the soil can affect the value of the corrosion rate. From the comparison of the sacrificial anode is resistant to corrosion Cr with the greatest corrosion rate 0.056 mpy on soil pH 7.36 and the smallest corrosion rate of 0.011 mpy on soil pH 7.98. As for the life time materials with protective anode longest Cr occurs at the anode is 6417.261 years then the material by using a sacrificial anode Mn has the smallest life time is 2223.303 years. Results were obtained by calculating Fundamentals of Metallic Corrosion and API 570. Keywords: cathodic protection, standart API 570, Fundamentals of Metallic Corrosion book, carbon steel API 5L Grade B, periodic inspection


Detil Peneliti

Dosen Pembimbing 1 :Endah Wismawati
Dosen Pembimbing 2 : Budi Prasojo

Program Studi : D4 - TEKNIK PERPIPAAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.