PENENTUAN JUMLAH DAN PENEMPATAN KLEM UNTUK MENGURANGI DEFORMASI PADA PIPA HEADER TS NPS 4 INCH SCHEDULE XXS

DETERMINATION OF NUMBER AND DISTANCE TO REDUCE DEFORMATION USING CLAMPS ON HEADER TS PIPE NPS 4 INCH SCHEDULE XXS

Sofyan Hanafi (6809040021)


Abstrak

Suatu deformasi pada sambungan pengelasan dapat merusakan material sehingga berakibat terjadinya misalignment terhadap komponen yang akan dipasang, hal ini terjadi tidak hanya pada plat namun juga bisa terjadi pada pipa yang mengalami penyambungan dengan pengelasan. Didalam metode ini analisis tegangan sisa yang terjadi dilakukan dengan cara menghitung beban panas akibat pengelasan kemudian menghitung besar gaya reaksi beban , hasil dari analisis software Ansys 12 dilakukan untuk mengetahui arah tegangan dan distribusi panas kemudian hasil perhitungan manual untuk mengetahui kebutuhan penumpu dan klem untuk mengurangi nilai distorsi. Dari nilai tegangan sisa yang telah didapatkan, pengelasan sambungan T Joint manifold dengan Pipa Header TS nps 4inch sch XXS yang berjumlah 4 buah maka semakin kecil perbedaan antara temperatur heat input pengelasan dan temperature pendinginan tersebut maka distorsi yang terjadi semakin kecil. hasil perhitungan manual menghasilkan perbedaan tegangan sisa disambungan 1 yaitu sebesar 412,52 Mpa, sambungan ke 2 yaitu 590,34 Mpa , sambungan ke 3 yaitu 685,90 Mpa, Sambungan ke 4 yaitu 453,48 Mpa ,perhitungan rancangan klem dan penumpu menghasilkan kekuatan untuk menopang berat pipa dan menahan tegangan yang berasal dari sambungan pengelasan , penumpu berjumlah 3 buah ,pada penumpu 1 dapat menumpu beban 84,695 Kg, penumpu ke 2 sebesar 192,657 Kg, penumpu 3 sebesar 84,695 Kg, 5 klem yang terpasang dengan beban yg didapat pada klem 1,2,4,5 sebesar 127,042 Kg ,klem ke 3 sebesar 288,985 Kg, hasil beban penumpu dan klem terbesar terdapat pada tengah bentangan pipa. Kata Kunci : deformasi,distorsi , misaligmen, beban panas , pengelasan , optimasi , penumpu , klem


Abstract

A deformation of the welding connection can damage the material that results in misalignment of the components to be installed, this happens not only at the plate but can also occur in connection with pipe welding experience. In this analysis method of residual stress that occurs is done by calculating the heat load due to welding and then calculate the reaction force of the load, the results of the analysis software Ansys 12 conducted to determine the direction of the voltage and heat distrbution then manual calculation to determine the need to reduce support and clamp value distortion. Residual stress values have been obtained, for welding T Joint manifold with TS Header Pipe NPS 4 inch sch XXS which consists of 4 pieces, the smaller the difference between the temperature of the welding heat input and the cooling temperatures of the distortion that occurs gets smaller. Manual calculations produce residual stress difference joint 1 is equal to 412,52 MPa, joint 2 is equal to 590,34 Mpa , joint 3 is equal to 685,90 MPa , joint 4 is equal to 453,48 MPa, design calculations of clamp and support have strength to support the weight of the pipe and from the welding, the support consists of 3 pieces, the support 1 cansustain load 84,695 Kg, support 2 cansustain load of 192,657 Kg , support 3 cansustain load 84,695 Kg, 5 clamps attached to that obtained at the expense 1, 2,4,5 at 127,042 Kg clamps, clamps 3 of 288,985 Kg, the biger load support and clamp results found in the middle of the largest stretch of pipe. Keywords: deformation, distortion, misaligmen, heat load, welding, optimization, support ,clamps?


Detil Peneliti

Dosen Pembimbing 1 :Muhammad Muhadi Eko Prayitno
Dosen Pembimbing 2 : Projek Priyonggo Sumangun

Program Studi : D4 - TEKNIK PERPIPAAN
Angkatan : 2009


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.