ANALISIS PENGARUH CHEMICAL INHIBITOR TERHADAP LAJU KOROSI MATERIAL SA 53 GRADE B AKIBAT CORROSION UNDER INSULATION

ANALYSIS THE EFFECT OF CHEMICAL INHIBITOR ON CORROSION RATE OF SA 53 GRADE B MATERIAL DUE TO CORROSION UNDER INSULATION

Aan Khamaludin (6809040003)


Abstrak

ABSTRAK Penelitian ini bertujuan untuk mengetahui perbandingan nilai laju korosi material SA 53 Grade B tanpa chemical inhibitor dengan material yang menggunakan chemical inhibitor karena pengaruh Corrosion Under Insulation dan nilai efisiensi penggunaan chemical inhibitor. Pengujian yang dilakukan mengacu pada ASTM G 189 Standard Guide for Laboratory Simulation of Corrosion Under Insulation. Aplikasi penggunaan chemical inhibitor adalah dengan mencampurkan ekstrak tembakau ke dalam campuran perlite yang digunakan sebagai insulation material. Metode perhitungan laju korosi menggunakan Mass Loss Method. Pada penelitian ini diperoleh nilai laju korosi sebesar 0.21086 mm/year, 0.19955 mm/year, 0.19783 mm/year untuk spesimen tanpa chemical inhibitor. Laju korosi material dengan chemical inhibitor adalah 0.11695 mm/year, 0.10779 mm/year dan 0.16251 mm/year. Nilai efisiensi penggunaan chemical inhibitor adalah 22.93 %, 45.98 % dan 40.88 % dengan nilai rata-rata efisiensi sebesar 36.60 %. Kata Kunci : Chemical Inhibitor, Corrosion Under Insulation, ASTM G 189, Mass Loss Method


Abstract

ABSTRACT The Purpose of this research is to determine the comparative value of the corrosion rate of SA 53 Grade B material without chemical inhibitors with material using chemical inhibitors for Corrosion Under Insulation influence and the efficiency of the use of chemical inhibitors. The simulation Tests were carried out referring to the ASTM G 189 Standard Guide for Laboratory Simulation of Corrosion Under Insulation. Application the use of chemical inhibitors with mixing tobacco extract to the mix perlite used for insulation material. Corrosion rate calculation methods using Mass Loss Method. In this research, the corrosion rate values obtained at 0.21086 mm/year, 0.19955 mm/year, 0.19783 mm/year for the specimen without chemical inhibitors. Corrosion rate material with a chemical inhibitor is 0.11695 mm/year, 0.10779 mm/year and 0.16251 mm/year. Values of the use of chemical inhibitors efficiency is 22.93%, 45.98% and 40.88% with a mean value of efficiency is 36.60%. Keywords: Chemical Inhibitor, Corrosion Under Insulation, ASTM G 189, Mass Loss Method


Detil Peneliti

Dosen Pembimbing 1 :Wiwik Dwi Pratiwi
Dosen Pembimbing 2 : George Endri K

Program Studi : D4 - TEKNIK PERPIPAAN
Angkatan : 2009


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.