ANALISIS VARIASI EXSPOSURE ANGLE PADA PENGUJIAN RADIOGRAFI UNTUK MENDETEKSI CACAT BUATAN TERHADAP KUALITAS FILM RADIOGRAFI PADA SAMBUNGAN CORNER JOINT

ANALYSIS OF EXPOSURE ANGLE VARIATION ON RADIOGRAPHY TEST TO DETECT ARTFICIAL DEFECT TO RADIOGRAPHY FILM QUALITY ON CORNER JOINT

Hendra Febriono (6712040063)


Abstrak

ABSTRAK Pengujian radiografi gamma ray adalah salah satu jenis metode pengujian tanpa merusak yang banyak diaplikasikan pada saat ini. Akan tetapi pengujian ini memiliki kekurangan, terutama pada exsposure sambungan corner joint. Dimana teknik penyinaran pada sambungan atau daerah corner joint sendiri terdapat beberapa daerah yang tidak tercover saat exsposure dilakukan. Teknik exsposure pada sambungan corner joint ini memunculkan kendala yaitu sulitnya mengidentifikasi kualitas film. Material baja karbon tipe SA 516 Gr 70 merupakan material yang digunakan untuk membuat produk sambungan corner joint. Dengan memvariasikan sudut exsposure dengan menggunakan sudut 15o, 30o, dan 45o maka diperoleh suatu hasil. Hasil tersebut akan dibuat refrensi dalam proses exsposure pada sambungan corner joint. Dari hasil pengujian diketahui bahwa hasil film dari exsposure menggunakan semua variasi sudut didapatkan perbedaan, dimana kualitas film pada sudut 15o memiliki densitas yang tidak memenuhi syarat. Pada sudut 30o dan 45o memiliki densitas yang memenuhi syarat dan ketentuan yang lain sesuai dengan standart. Dan selisih ukuran citra diskontinuitas pada film radiografi terhadap ukuran sebenarnya yaitu : 15o = 0,12 mm dan 0,15 mm, 30o = 0,30 mm dan 0,35 mm, 45o = 0,45 mm dan 0,50 mm. Selisih pada cacat tidak melebihi nilai yang sudah ditentukan standart yaitu 0,51 mm. Kata kunci : radiografi gamma ray, corner joint, cacat buatan, variasi sudut


Abstract

ABSTRACT Gamma ray radiographic testing is one type of non destructive test methods widely apllied at this time. However, this testing has some weakness, especially for the exposure at corner joint. Where the technique of exposure on the weld joint or corner joint area itself has some area that uncover when the exposure is done. The exposure technique on the corner joint make some obstacles that is the difficulty to identify the film quality. Carbon steel material types SA 516 Gr 70 is a material used to produce corner joint. With varying the exposure angle by using the angle of 15o, 30o, and 45o so obtained a result. That result will be a reference on exposure process at corner joint. From the result is known that the film from the exposure using all variation of angle obtained a different, where the film quality at an angle of 15o has density not accordance with the standard. At the angle of 30o and 40o have density that fulfill to the requirement and other provision that accordance to the standard. And the difference size of discontinuity image from the radiography film to actual size that are : 15o = 0,12 mm and 0,15 mm, 30o = 0,30 mm and 0,35 mm, 45o = 0,45 mm and 0,50 mm. Differencess in the defect does not exceed from the value that has determined on standard is 0,51 mm. Keywords : gamma ray radiography, corner joint, artficial defect, angle variation


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : Hendri Budi K.

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.