PENGARUH KUAT ARUS DAN PULSE WIDTH PADA PENGELASAN ALUMINIUM 5083 POSISI 3G VERTICAL DOWN DENGAN PROSES GMAW MODE SUPERPULS TERHADAP STRUKTUR MAKRO DAN SIFAT MEKANIS

INFLUENCE OF CURRENT AND PULSE WIDTH IN WELDING ALUMINIUM 5083 WITH 3G VERTICAL DOWN POSITION BY USED GMAW MODE SUPERPULS PROCESS ABOUT MACRO STRUCTURE AND MECHANICAL PROPERTIES

Bagus Rahman Setiawan (6712040059)


Abstrak

Saat ini produksi kapal aluminium mulai banyak dibuat seperti pada kapal perang dan kapal FPB (Fast Patrol Boat). Pada kapal terutama pada bagian webframe kapal, bagian double bottom, dan bagian kamar mesin sangat diperhitungkan karena pada bagian yang memerlukan full weld banyak terkena tegangan yang cukup besar. Penelitian ini dilakukan dengan tujuan untuk mengetahui struktur makro dan pengelasan Aluminium tipe 5083 dengan sambungan tumpul (Butt Joint) dengan dilakukan posisi pengelasan 3G vertical down dengan variasi kuat arus 130 A, 140 A, 160 A dan variasi waktu Superpuls (Pulse width) 0.1, 0.3, dan 0.5 detik. Berdasarkan hasil pengujian tarik paling tinggi terdapat pada spesimen dengan kuat arus 160 A waktu pulse width (superpuls) 0,1 detik sebesar 271,35 Mpa dan untuk spesimen dengan kekuatan tarik paling rendah yaitu pada spesimen dengan kuat arus 130 A dan waktu pulse width (superpuls) 0,1 detik sebesar. Sedangkan pengujian makro didapatkan persentase delusi tertinggi dengan kuat arus 160 A dengan waktu superpuls 0.1 detik yaitu 34% dan persentase delusi terendah dengan kuat arus 130 A dengan waktu super pulse 0.1 detik yaitu 25%. Kata kunci : Aluminium 5083, 3G Vertical Down, Pulse Width / Superpuls, GMAW, Uji Tarik, Uji Makro,


Abstract

Currently the production of aluminum?s ship begin make a lot such as warships and FPB (Fast Patrol Boat). On the ships, especially on the part of webframe, part of a double bottom, and part of the engine room is very calculate because the part that requires a full weld expose heavily the large stresses. This research have purpose to find out the macro structure and mechanical properties of welding Aluminium type 5083 with connection (Butt Joint) to do welding position of 3G vertical down with variations current is 130 A, 140 A, 160 A and the variation time of Superpuls (Pulse width) is 0.1, 0.3, and 0.5 seconds. Based on the results of the most tensile test found in the currents of 160 A and pulse width time (superpuls) 0.1 seconds with value 271.35 MPa and for the specimen with lowest tensile strength in the specimen with currents 130 A and pulse width time (superpuls) 0.1 seconds is value 211,05 Mpa. Meanhile, macro test highest percentage delusions obtained by the current 160 A with superpuls time 0.1 seconds is 34% and the lowest percentage delusions of the currents 130 A with superpuls time of 0.1 seconds is 25%. Keyword : Aluminum 5083, 3G Vertical Down, Pulse Width / Superpuls, GMAW, Tensile Test, Macro Test.


Detil Peneliti

Dosen Pembimbing 1 :Bachtiar
Dosen Pembimbing 2 : Moch. Karim Al Amin

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.