ANALISA PENGELASAN OVER HEAT INPUT PADA MATERIAL AUSTENITIC STAINLESS STEEL SA 312 TIPE 316 DENGAN KEEFEKTIFAN PASCA PENDINGINAN DAN CHEMICAL SURFACE TREATMENT TERHADAP NILAI KEKERASAN DAN PITTING CORROSION

Analysis of over heat input welding on austenitic stainless steel sa 312 type 316 materials with the eefectiveness of post-cooling and chemical surface treatment to the value of violence and pitting corrosion

Muhammad Yusron Alfany (6712040058)


Abstrak

Pada pengelasan GTAW (Gas Tungsten Arc Welding) terdapat dua masukan panas (heat input) yang digunakan yaitu diatas 2.0 kJ/mm dan dibawah 2.0 kJ/mm. Setelah pengelasan tersebut dilakukan proses pendinginan quenching dan ambient untuk menjaga ketahanannya terhadap korosi pitting dan nilai kekerasan material tersebut. Serta dilakukan chemical surface treatment untuk membersihkan oxide scale pada permukaan yang menyebabkan daerah tersebut kekurangan kromium, sehingga mempengaruhi ketahanan korosi menurun pada pengelasan pipa stainless steel. Dilakukan penelitian bagaimana nilai kekerasan hasil pengelasan antara heat input diatas 2.0 kJ/mm dan dibawah 2.0 kJ/mm, serta ketahanannya terhadap korosi pitting. Penelitian heat input diatas 2.0 kJ/mm dan dibawah 2.0 kJ/mm menggunakan material pipa SA 312 tipe 316. Penelitian dilakukan dengan mngetahui hasil nilai uji hardness vickers dan uji korosi pitting dengan metode sel tiga elektroda yang diberi ke dua proses pendinginan ditambah chemical surface treatment. Dari hasil uji hardness vickers, diketahui bahwa heat input diatas 2.0 kJ/mm memiliki kekerasan lebih rendah dibandingkan heat input dibawah 2.0 kJ/mm. Dari semua nilai kekerasan yang diperoleh material tersebut semakin menurun dikarenakan unsur persipitasi karbida berkurang. Dari hasil pengujian korosi pitting didapatkan nilai laju korosi heat input diatas 2.0 kJ/mm sebesar 0.222, 0.225, 0.274, dan 0.332 mmpy. Dan nilai laju korosi heat input dibawah 2.0 kJ/mm sebesar 0.341, 0.389, 0.448, dan 0.478 mmpy. Dari semua nilai laju korosi yang diperoleh material tersebut masuk dalam kategori good. Kata kunci : GTAW, over heat input, quenching, ambient, chemical surface treatment, hardness vickers, korosi pitting, sel tiga elektroda


Abstract

In welding GTAW (Gas Tungsten Arc Welding) there are two heat input (heat input) used is above 2.0 kJ / mm and below 2.0 kJ / mm. After the welding process is carried out quenching and ambient cooling to keep the resistance to pitting corrosion and the hardness of the material. And conducted chemical surface treatment to clean the oxide scale on the surface which leads to chromium deficiency, thus affecting the corrosion resistance decreased in welding stainless steel pipe. Conducted research into how the hardness value between heat input welding results above 2.0 kJ / mm and below 2.0 kJ / mm, as well as its resistance to pitting corrosion. Research heat input above 2.0 kJ / mm and below 2.0 kJ / mm using pipe material SA 312 316. The type of research is done by knowing the results of the vickers hardness test and pitting corrosion test by the method of three-electrode cell by the second cooling process plus chemical surface treatment , Vickers hardness of the test results, it is known that the heat input above 2.0 kJ / mm has a lower hardness than the heat input below 2.0 kJ / mm. Of all the material hardness values obtained are decreased due to reduced carbide persipitasi elements. From the test results obtained pitting corrosion rate of heat input values above 2.0 kJ / mm for 0222, 0225, 0274, and 0332 mmpy. And the corrosion rate of heat input values below 2.0 kJ / mm for 0341, 0389, 0448, and 0478 mmpy. Of all the corrosion rate values obtained material falls within the category of good. Keywords: GTAW, over heat input, quenching, ambient, chemical surface treatment, vickers hardness, corrosion pitting, three-electrode cell


Detil Peneliti

Dosen Pembimbing 1 :Muhamad Ari
Dosen Pembimbing 2 : Adhi Setiawan

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.