PENGARUH VARIASI TEMPERATUR PREHEAT TERHADAP STRUKTUR MIKRO DAN KEKERASAN PENGELASAN FCAW V BRACKET DAN STERNTUBE YANG MENGALAMI HOT CRACK

THE INFLUENCE PREHEAT TEMPERATURE VARIATION ON MICROSTRUCTURE AND FCAW V BRACKET HARDNESS WELDING AND STERN TUBE HOT CRACKING

Dandy Bintarfano Dwinanda (6712040057)


Abstrak

PENGARUH VARIASI TEMPERATUR PREHEAT TERHADAP STRUKTUR MIKRO DAN KEKERASAN PENGELASAN FCAW V BRACKET DAN STERNTUBE YANG MENGALAMI HOT CRACK Nama : Dandy Bintarfano Dwinanda NRP : 6712040057 Program Studi : Teknik Pengelasan Dosen pembimbing : 1. Mohammad Thoriq Wahyudi, ST., MM. 2. Moh. Syaiful Amri, S.ST., MT ABSTRAK V bracket dan sterntube merupakan salah satu penunjang pada bagian bangunan kapal dimana v bracket menggunakan material KI grade D dan sterntube menggunakan material grey cast iron G2500a, dimana untuk material grey cast iron G2500a ini memiliki kadar karbon yang tinggi (lebih dari 2%) menyebabkan logam ini sangat sulit untuk dilas seperti pada logam pada umumnya. maka diperlukannya suatu perlakuan khusus dan elektroda yang khusus untuk mendapatkan hasil lasan yang baik. Pada penelitian ini bertujuan untuk menganalisa pengaruh suhu preheat terhadap struktur mikro dan kekerasan pengelasan KI grade D dengan grey cast iron G2500a yang mengalami hot crack. Proses pengelasan pada penelitian ini menggunakan pengelasan full FCAW dan pengelasan kombinasi antara SMAW menggunakan elektroda ENiFe-Cl dan FCAW menggunakan elektroda E71T-1. Dalam penelitian ini juga dilakukan beberapa variasi perlakuan suhu preheat yakni 200?C, 250?C, 350?, 400?C. Dari pengujian penetrant test tampak bahwa pengelasan full FCAW dengan variasi suhu preheat 200?C dan 250?C selalu timbul linear crack sepanjang 150 mm di daerah toe, sedangkan pada pengelasan kombinasi antara SMAW dan FCAW pada weld metal ENiFe-Cl dengan variasi suhu preheat 200?C, 250?C, 350?, 400?C tidak ada indikasi keretakan akan teteapi retak timbul pada batas weld metal ENiFe-Cl dan weld metal E71T-1. Berdasarkan hasil struktur mikro diketahui bahwa adanya preheat dengan suhu yang semakin tinggi dapat mengurangi terjadinya struktur yang keras (ferrite dan grafit yang besar) pada daerah HAZ. Nilai kekerasan HAZ menurun seiring dengan bertambahnya temperatur preheat. Kata kunci : KI grade D, Grey cast iron G2500a, preheat, elektoda E71T-1, elektroda ENiFe-Cl


Abstract

INFLUENCE PREHEAT TEMPERATURE ON MICROSTRUCTURE AND HARDNESS OF WELDING FCAW V BRACKET AND STERNTUBE ARE EXPERIENCING HOT CRACK Written by : Dandy Bintarfano Dwinanda NRP : 6712040057 Study program : Teknik Pengelasan Advisors : 1. Mohammad Thoriq Wahyudi, ST., MM. 2. Moh. Syaiful Amri, S.ST., MT ABSTRACT V bracket and sterntube is one of support on the part of ship building where v bracket using materials KI grade D and sterntube using the material of gray cast iron G2500a, which for material gray cast iron G2500a has a high carbon content (over 2%) causing the metal this is very difficult to weld like on metal in general. hence the need for a special treatment and special electrodes to obtain a good weld results. In this study aims to analyze the influence of preheat temperature on the microstructure and hardness KI grade D welding of gray cast iron with G2500a experiencing hot crack. The welding process on this peneitian using full welding FCAW and SMAW welding uses a combination of electrode ENiFe-Cl and FCAW electrodes E71T-1. In this study also do some treatment variations preheat temperature that is 200 ? C, 250 ? C, 350 ?, 400 ? C. From testing penetrant test it appears that the welding full FCAW with temperature variations preheat to 200 ? C dan250 ? C always arise linear crack along 150 mm in the toe, while the welding combination of SMAW and FCAW on weld metal ENiFe-Cl with temperature variations preheat to 200 ? C , 250 ? C, 350 ?, 400 ? C there is no indication of the cracks will arise at the boundaries teteapi cracked weld metal and weld metal ENiFe-Cl E71T-1. Based on the results of the microstructure is known that the preheat with the higher temperatures can reduce the occurrence of a hard structure (ferrite and graphite were great) in HAZ area. HAZ hardness values decreased with increasing preheat temperature. Keywords: KI grade D, Grey cast iron G2500a, preheat, E71T-1 electrode, the electrode ENiFe-Cl


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : M.Syaiful Amri

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012