PT.X sebagai perusahaan BUMN di bidang produksi kereta api di indonesia mendapat sebuah pesanan gerbong kereta api dari bangladesh. Pada proses fabrikasinya terdapat metode pengelasan menggunakan spot welding. Seelah dilakukan pengelasan terjadi korosi di daerah lasan tersebut sehingga perlu dilakukan penelitian tentang parameter pengelasan spot welding terhadap serangan korosi tersebut. Penelitian ini akan melakukan variasi kuat arus dan waktu terhadap laju korosi dengan melakukan pengujian elektrokimia (sel tiga elektroda) sesuai ASTM G 3 dan ASTM G 102 dengan larutan uji berupa NaCl (Natrium Klorida). Pengujian ini difokuskan di daerah weld metalsaja. Hasil pengujian laju korosi dapat disimpulkan bahwa spesimen yang menggunakan kuat arus yang lebih tinggi mempunyai sifat ketahanan korosi yang lebih tinggi daripada spesimen yang menggunakan kuat arus yang rendah. Tidak ada pengaruh weld time terhadap laju korosi pada proses spot welding.Kandungan NaCl sebesar 3,5% mempunyai nilai laju korosi lebih besar daripada kandungan NaCl sebesar 10%. Kandungan NaCl berpengaruh sebesar 49,81% terhadap laju korosi. Kata kunci :Resistance spot welding, Kuat arus


Abstract

PT.X as a state-owned company in the field of rail production in indonesia received an order from bangladesh railway carriage. In the fabrication process there is a welding method using spot welding. After welding corrosion in the weld area that needs to be done reseach about paramaters spot welding against the corrosion attack. This study will variance current and weld time of the corrosion rate (three electrode cells) according to ASTM G 3 by testing ASTM G 102 with a test solution NaCl (Sodium Chloride). This test is focused in the area of weld metal only. The test result can be concluded that the corrosion rate of specimens that uses high currents which have high corrosion tesistance properties higher than specimens using powerful low current. No influence weld time corrosion rate of spot welding process. NaCl content of 3,5% has a value higher than the corrosion rate of NaCl content 10%. Effect of NaCl content of 49,81% on the corrosion rate. Keywords: Resistance Spot welding, Current


Detil Peneliti

Dosen Pembimbing 1 :Mukhlis
Dosen Pembimbing 2 : M.Syaiful Amri

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.