STUDI PENGARUH VARIASI SUHU RUANG PADA PENGELASAN TUBE SB 338 ? Gr 1 TO TUBESHEET SB 265 ? Gr 1 (CLADDING) DENGAN PROSES GTAW TERHADAP KUALITAS HASIL METALOGRAFI DAN KEKERASAN

STUDY OF THE INFLUENCE OF ROOM TEMPERATURE VARIATION ON WELDING OF TUBE SB 338 ? Gr1 TO TUBESHEET SB 265 ? Gr1 (CLADDING) WITH GTAW PROCESS TO METALLOGRAPHIC AND HARDNESS QUALITY

Wahid Syifaur Rahman (6712040051)


Abstrak

ABSTRAK Pada on the job training di PT. Adhi Karya proyek PLTU 2 X 110 MW Balikpapan sedang dilakukan proses pembuatan condenser. Condenser tersebut menggunakan material titanium tube SB 338 - Gr1 dan tubesheet SB 265 -Gr1. Hasil pengelasan material titanium SB 338 - Gr1 dan tubesheet SB 265 -Gr1 sangat sensitive pada perubahan suhu ruang. Cacat seperti porosity, crack, under cut, slag inclusion, atau cacat-cacat lain yang kemungkinan bias terjadi. Dibutuhkan metode khusus dalam mengatur suhu ruang seperti penggunaan AC (air condition) pada saat proses pengelasan untuk mendapatkan suhu ruang yang diinginkan. Maka dilakukan penelitian untuk mengetahui hasil pengelasan material titanium tube SB 338 - Gr1 dan tubesheet SB 265 -Gr1 dengan beberapa variasi. Variasi tersebut antara lain menggunakan suhu ruang 34.6?C, 30.1?C dan 25.0?C. Untuk mengetahui perbedaannya maka dilakukan uji metalografi makro, metalografi mikro dan kekerasan. Hasil pengujian metalografi makro dan mikro yang didapatkan menunjukan bahwa tidak terjadi perbedaan yang signifikan pada variasi suhu ruang saat pengelasan. Pada pengujian metalografi makro, semua hasil pengelasan menunjukkan fusi yang sempurnah dan tidak ditemukan cacat pengelasan. Pengujian metalografi mikro menunjukkan pada daerah weld metal fasa beta mendominasi, sedangkan pada base metal terdapat fasa alpha yang dominan. Pada pengujian kekerasan didapatkan nilai rata-rata tertinggi pada variasi suhu ruang 34.6 ?C sebesar 229.3 HVN, 30.1 ?C sebesar 228.95 HVN, dan 25.0 ?C sebesar 228.3 HVN. Kata kunci: Titanium, variasi suhu ruang, uji mekanis, struktur mikro, SB 265 Grade 1, SB 338 Grade 1.


Abstract

ABSTRACT During on the job training in PT. Adhi Karya PLTU 2 X 110 MW Balikpapan project had made condenser. That condenser use titanium tube SB 338 - Gr1 dan tubesheet SB 265 -Gr1 materials. The result of titanium tube SB 338 - Gr1 dan tubesheet SB 265 -Gr1 welding is very sensitive to the change of room temperature. The discontinuity are likes porosity, crack, under cut, slag inclusion, or others discontinuity can happens. Need some specific metods like using AC(air conditioner) when the welding process to get room temperate that needed. So doing experiment to know the titanium tube SB 338 - Gr1 and tubesheet SB 265 -Gr1 welding result with some variations. That variations are using room temperatures 34.6?C, 30.1?C and 25.0?C. To know the deferens of the result so metalugraphy makro, metalugraphy mikro, and hardness test have doing. The result of melugraphy macro and micro that got showed that no any significant different on the variation room temperature during weld. On metalugraphy macro test showed that all the result of welding have perfect fusion and no discontinuity. The metalugraphy micro test showed that weld metal area dominated by beta phase, and on base metal area dominated by alpha phase. On hardness test have got the higger average amont 229.3 HVN at the room temperature 34.6 ?C, 228.95 HVN at the temperature 30.1 ?C, and 228.3 HVN at the temperature 25.0 ?C. Keywords: Titanium, room temperature variation, mechanical test, microstructure, Grade 1 SB 265, SB 338 Grade 1.


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : M.Syaiful Amri

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012