PENGARUH VARIASI MIXTURED SHIELDING GAS PENGELASAN GMAW PADA MATERIAL FERRITIC STAINLESS STEEL TIPE DIN 1.4003 TERHADAP STRUKTUR MIKRO, SIFAT MEKANIK DAN FERRITE CONTAIN DI PT.INKA

THE EFFECT OF GMAW WELDING MIXTURED SHEILDING GAS VARIATION ON FERRITIC STAINLESS STEEL MATERIAL OF DIN 1.4003 TYPE THROUGH MICRO STRUCTURE, MECHANICAL FORM AND FERRITE CONTAIN AT PT. INKA

Mohammad Afif As'ari (6712040048)


Abstrak

PENGARUH VARIASI MIXTURED SHIELDING GAS PENGELASAN GMAW PADA MATERIAL FERRITIC STAINLESS STEEL TIPE DIN 1.4003 TERHADAP STRUKTUR MIKRO, SIFAT MEKANIK DAN FERRITE CONTAIN DI PT.INKA Nama : Mohammad Afif Asari Pembimbing : 1. Mohammad Thoriq Wahyudi, ST.,MM 2. Hendri Budi Kurniyanto., S.ST., M.T ABSTRAK Shielding Gas adalah suatu gas pelindung pada proses pengelasan GMAW (Gas Metal Arc Welding) untuk mempertahankan atau menjaga stabilitas busur dan perlindungan cairan logam las dari kontaminasi selama pengelasan pada daerah las. Dalam prosesnya gas pelindung mempunyai berbagai macam jenis gas dimana pada standard/code diatur jika perubahan gas pelindung adalah essential variable yang jika dirubah akan membuat sifat mekanisnya berubah. Pada tugas akhir ini menggunakan 2 jenis gas yang berbeda yaitu Ar 97,5% CO2 2,5% dan Ar 98% O2 2% yang akan di aplikasikan pada side wall kereta api di PT.INKA. Proses pengelasan ini dilakukan dengan beberapa prosedur pengelasan dan pengujian yang akan dilakukan. Langkah awal yaitu dengan melakukan proses pengelasan sesuai WPS yang ada dengan menggunakan 2 jenis gas yang berbeda dimana dibagi menjadi 3 joint jenis gas. Setelah proses pengelasan selesai dilakukan beberapa pengujian yaitu uji visual, uji radiografi, uji tarik, uji lengkung, uji ferrite contain, uji makro dan mikro, uji raw material dan uji komposisi kimia. Proses penelitian ini di ketahui jika menggunakan gas pelindung Ar 97,5% O2 2,5% mempunyai rata-rata nilai kuat tarik yang tinggi sebesar 471,75 MPa dibanding gas pelindung Ar 97,5% CO2 2,5% sebesar 455,62 MPa. Hasil uji makro Hasil uji makro menghasilkan sambungan las yang fusi dan rata-rata presentase dilusi pada penggunaan gas pelindung Ar 97,5% CO2 2,5% sebesar 16,94% dan penggunaan gas pelindung Ar 97,5% O2 2,5% sebesar 17,31%, hasil uji mikro menghasilkan struktur intinya berbentuk serat, terdiri dari austenite (putih) dan delta ferrite (bagian hitam) pada batas dendritik. Hasil uji ferrite contain menghasilkan rata-rata presentase ferrite yang berbeda pada 2 jenis gas pelindung yang digunakan, yaitu sebesar 7,1% untuk gas pelindung Ar 97,5% CO2 2,5% dan 7,8% untuk gas pelindung Ar 97,5% O2 2,5%. Kata kunci: Shielding gas, argon, karbondioksida, okigen, ferritic ss DIN 1.4003


Abstract

THE EFFECT OF GMAW WELDING MIXTURED SHEILDING GAS VARIATION ON FERRITIC STAINLESS STEEL MATERIAL OF DIN 1.4003 TYPE THROUGH MICRO STRUCTURE, MECHANICAL FORM AND FERRITE CONTAIN AT PT. INKA Name : Mohammad Afif Asari Advisor : 1. Mohammad Thoriq Wahyudi, ST.,MM 2. Hendri Budi Kurniyanto., S.ST., M.T ABSTRACT Sheilding gas is a defensive gas for welding process of GMAW ( Gas Metal Arc Welding) in order to defend or keep the arc stability and protect the liquid weld metal from contanitaion thru the weliding process around weld area. In the process of sheilding gas has a variety gas where is settled on the standar/code if the sheilding gas changes into an essential variable which will change its mechanical form if it is reformed. This last project uses two different kind of gas that is Ar 97.5% CO2 2.5% and Ar 8% O2 2% which will be mounted on side wall of train at PT. INKA. This welding process is done with some procedures and the test which will be done. The beginning step does the welding process a line with the existed WPS which uses two different kind of gas in which are divided into three joint point of gas. After finishing the welding process is done some test which is visual, radiography, pulling, bend, ferrite contain, macro and micro, raw material and chemical composition test. This research process is identified if the welding process uses the shielding gas of Ar 97.5% O2 2.5%, it will have an average of tensile strength values mount 471.75 MPa compared with the shielding gas of Ar 97.5% CO2 2.5% mount 455,62 MPa. The macro test results the fusion welded joints and has a dilution average on using of shielding gas of Ar 97.5% CO2 2.5% about 16.94% and shielding gas of Ar 975% O2 25% about 17.31%. The micro test results its main structure to be fiber shape which contains of austenite (white side) and delta ferrite (black side) on dendritic limit. The ferrite contain results different ferrite percentage average on two kinds of shielding gas which are used, it is about 7.1% for shielding gas of Ar 97.5% CO2 2.5% and 7.8% for shielding gas of Ar 97.5% O2 2.5%. Keyword: shielding gas, argon, carbon dioxide, oxygen, ferritin ss DIN 1.4003


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : Hendri Budi K.

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.