ANALISA VARIASI TEMPERATUR PWHT DAN HOLDING TIME PADA MATERIAL SA 283 GR C TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO, PROJECT DRYER 03 M 362 DI PT. PETROKIMIA GRESIK

ANALYSIS OF PWHT TEMPERATURE VARIANT AND HOLDING TIME INTO SA 283 GR C MATERIAL ON MECHANICAL PROPERTIES AND MICROSTRUCTURE, DRYER 03 M 362 PROJECT IN PT. PETROKIMIA GRESIK

Hendy Kurniawan Pratama (6712040047)


Abstrak

Dari sekian banyak produksi yang dihasilkan Departemen Fabrikasi PT. Petrokimia Gresik, salah satunya adalah mesin dryer atau mesin pengering pupuk tipe 03 M 362 yang sedang mengalami proses pengerjaan. Dalam hal ini salah satu proses yang perlu diperhatikan adalah proses PWHT (Post Weld Heat Treatment). Dalam penelitian ini metode yang akan digunakan adalah stress relief annealing. Stress relief annealing adalah dimana temperatur pemanasannya tidak mencapai temperatur A1. Temperatur PWHT dan holding time yang akan digunakan dalam penelitian ini adalah temperatur 595?C dengan holding time selama 60 dan 96 menit, temperatur 625?C dengan holding time selama 60 dan 96 menit, dan temperatur 700?C dengan holding time selama 60 dan 96 menit. Dari data uji kekerasan disimpulkan bahwa semakin tinggi temperatur PWHT dan semakin lama holding time maka nilai kekerasan juga semakin menurun, hal ini dikarenakan dengan pemanasan tinggi dan pendinginan yang lambat dapat membuat struktur material lebih lunak. Dari data uji tarik maka dapat disimpulkan bahwa semakin tinggi temperatur maka nilai kuat tarik juga semakin turun, namun apabila holding time semakin lama maka kuat tarik akan semakin tinggi. Hal ini disebabkan holding time memberikan waktu untuk karbon berdifusi, sehingga kuat tarik semakin tinggi dan struktur menjadi lebih halus. Kata kunci : Post Weld Heat Treatment, annealing, stress relief annealing, holding time


Abstract

Of the many production fabrication department of PT. Petrokimia Gresik, which is a machine dryer or driying machine fertilizer the types is 03 M 362 still in undergoing construction. In this case one of the processes PWHT (Post Weld Heat Treatment). In this research, the method that will be used is the stress relief annealing. Stress relief annealing is where the heating temperature does not reach the temperature A1. The temperature PWHT and holding time to be used in this research is the temperature of 595?C with a holding time for 60 and 96 minutes, a temperature of 625?C with a holding time for 60 and 96 minutes, and a temperature of 700?C with a holding time for60 and 96 minutes. From the test data concluded that the higher hardness PWHT temperature and the longer holding time will decrease the value of violence, this is because with high heating and slow cooling rate to make the structure more malleable material. From the tensile test data it can be concluded that the higher that the temperature, the tensile strength values are also getting down, but if the longer the holding time will be higher tensile strength. This is due to holding time to allow time for the carbon diffuses, so that higher tensile strength and the structure becomes smooth. Keywords : Post Weld Heat Treatment, annealing, stress relief annealing, holding time


Detil Peneliti

Dosen Pembimbing 1 :Muhamad Ari
Dosen Pembimbing 2 : Imam Khoirul Rohmat

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.