PENGARUH VARIASI KECEPATAN ALIRAN FLUIDA TERHADAP STRUKTUR MIKRO, NILAI KEKERASAN DAN LAJU KOROSI PADA PENGELASAN DOUBLING PLATE

VARIATION FLOW RATE SPEED FLUIDA EFFECT TO MICRO STRUCTURE, HARDNESS TEST AND CORROSION RATE AT DOUBLING PLATE WELDING

Ahmad Nasrullahi (6712040046)


Abstrak

PENGARUH VARIASI KECEPATAN ALIRAN FLUIDA TERHADAP STRUKTUR MIKRO, NILAI KEKERASAN DAN LAJU KOROSI PADA PENGELASAN DOUBLING PLATE Oleh AHMAD NASRULLAHI NRP : 6712040046 ABSTRAK Doubling Plate merupakan metode maintenance atau repair yang proses motodenya hampir sama dengan metode sleeve welding yang biasa di aplikasikan di in-service pipe line atau piping system. Metode ini di aplikasikan jika pipe line atau piping system mengalami kerusakan minor seperti internal corrosion yang di akibatkan tebal dari pipa berkurang dari tebal minimum yang di persyaratkan dan external corrosion yang biasanya di akibatkan dari faktor lingkungan atau human error. Sehingga metode ini dilakukan untuk menambah umur operasi dari pipa tersebut. Dalam penelitian ini menggunakan material pipa API 5L grade B NPS 4 sch 40 pada pipa Induk sedangkan material yang digunakan pada doubling plate API 5L grade B NPS 5 sch 40 dengan ketebalan 6 mm. Proses pengelasan dilakukan dengan metode SMAW dengan menggunakan elektroda E7018 dengan memvariasikan flow rate 0 LPM (Liter Per Minute), 2 LPM (Liter Per Minute), 4 LPM (Liter Per Minute). Dari data uji kekerasan, dengan semakin cepat flow rate hasil kekerasannya semakin meningkat juga. Hal tersebut di akibatkan oleh adanya kecepatan air yang berbeda dan proses pendinginan cepat (quench) yang mengakibatkan oleh adanaya perbedaan dari variasi flow rate tersebut. Sedangkan jika di lihat dari data laju korosi semakin cepat flow rate fluida maka hasil laju korosi yang di hasilkan juga semakin tinggi. Hal tersebut juga di karenakan adanya proses transfer massa pada antar muka logam atau fluida. Kata-kata kunci : doubling plate, in-service pipelines, SMAW


Abstract

VARIATION FLOW RATE SPEED FLUIDA EFFECT TO MICRO STRUCTURE, HARDNESS TEST AND CORROSION RATE AT DOUBLING PLATE WELDING Oleh AHMAD NASRULLAHI NRP : 6712040046 ABSTRACT Doubling Plate is a method of maintenance or repair that motodenya process is similar to the sleeve welding method commonly applied in the in-service pipe line or piping system. This method is applied if the pipe line or piping system suffered minor damage such as internal corrosion that causes reduced thickness of the pipe of minimum requisite thickness and external corrosion are usually in result of environmental factors or human error. So the method is carried out to increase the operating life time of the pipeline. In this study using the pipe material API 5L grade B NPS 4 sch 40 in the mains pipe while the materials used in the doubling plate API 5L grade B NPS 5 sch 40 with a thickness of 6 mm. Welding process is done with the SMAW method using E7018 electrode by varying the flow rate of 0 LPM (Liters Per Minute), 2 LPM (Liters Per Minute), 4 LPM (Liters Per Minute). From the hardness test data, with the faster flow rate increased hardness results as well. It is by comparing the different speed of the water and the rapid cooling (quench) that result by the difference of the flow rate variations. Meanwhile, if in view of the corrosion rate data faster fluid flow rate, the results of corrosion rate is derived also higher. It is also because of the mass transfer process on metal or fluid interface. Keywords : doubling plate, in-service pipelines, SMAW


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : Usman Dinata

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.