DESAIN WELDING PROSEDUR PENGELASAN HARDFACING MATERIAL DUPLEX STAINLESS STEEL MENGGUNAKAN ELEKTRODA HARDFACING TUBULAR TFe20 PADA SCREW CSU

DESIGN WELDING PROCEDURE HARDFACING WELDING MATERIAL DUPLEX STAINLESS STEEL WITH USE ELECTRODE HARDFACING TUBULAR TFe20 ON SCREW CSU

Aldi Cahya Firdaus (6712040045)


Abstrak

Proses hardfacing overlay sangat diperlukan pada maintenance screw CSU agar blade screw tidak mengalami keausan. Saat ini elektroda hardfacing SMAW menggunakan NS8838 dan mengalami keterbatasan stok oleh karena itu perlu dicoba elektroda yang sejenis yaitu elektroda hardfacing tubular TFe20. Namun demikian sebelum diaplikasikan perlu dilakukan kualifikasi terlebih dahulu untuk kelayakan produk baru tersebut. Pada penelitian kali ini yang menjadi variasi adalah arus. Proses pengelasan yang dilakukan menggunakan dua layer sesuai permintaan client spec sebagai perhatian utama. pengelasan pada layer pertama seluruhnya menggunakan arus 110A, terdapat empat variasi arus las yang digunakan pada layer kedua yaitu 110A sama dengan layer pertama, 70A (-30% dari layer pertama), 120A ( 10% dari layer pertama), dan 150A ( 30% dari layer pertama). Pengujian yang dilakukan pada spesimen tersebut meliputi uji liquid penetrant, metalografi (makrografi untuk mengetahui dilusi dan struktur mikro), hardness, dan uji komposisi kimia. Dari hasil pengujianliquid penetrant semua spesimen menunjukan adanya crack dan porosity, serta pada pengujian makrografi menunjukan semua spesimen mengalami crack dan porosity pada potongan melintang. Untuk nilai kekerasan spesimen pengelasan layer kedua 150A ( 30% dari layer pertama) memiliki nilai kekerasan tertinggi yaitu 657 HVN sedangkan nilai kekerasan terendah yaitu 532 HVNuntuk spesimen pengelasan layer kedua 70A (-30% dari layer pertama). Pada uji komposisi kimia deposit las spesimen didominasi oleh unsur kromium (Cr) sekitar 13% sampai 17% dan kandungan karbon (C) lebih dari 4%, maka struktur yang terbentuk adalah massive primary carbide didalam matrix austenite-carbide eutectic. Kata kunci : Hardfacing, elektroda TFe20, SMAW, heat input.


Abstract

Hardfacing overlay is importance on CSU screws maintenance that screwsblade not suffering from wear. Now hardfacing electrode use NS8838 and limited stock therefore necessary to try similar electrodes are tubular hardfacing electrodes TFe20. However, prior to application needs to to be qualified prior to the feasibility of the new product On this research that become the variable is amperage.Welding process use two layers overlays according the client specification with second layer as primary attention. There are four in variation, the second layer of first specimen use amperage 110A, the second layer of second specimen use amperage 70A (-30% from first layer), the second layer of third specimen use amperage 120A ( 10% from first layer), and the second layer of forth specimen use amperage 150A ( 30% from first layer). At all first layer using amperage 110A. The testing of specimens are liquid penetrant, metallography, hardness, and chemical compotition. From the result of testing for liquid penetrant testing show check cracking and porosity at all specimen. For the metallograpy testing show crack and porosity on cross section at all specimen. The highest hardness value is 657 HVN for the spesimen with variable 150A ( >30% from first layer), meanwhile The lowest hardness value is 532 HVN for the spesimen with variable 70A (->30% from first layer). For the chemical composition testing of weld deposit are spesimen dominated chromium(Cr) around 13% - 17% and carbon(C) more than 4%, so the microstructure that formed is massive primary carbide in matrix austenite-carbide eutectic. Keyword : Hardfacing, electrode TFe20, SMAW, heat input.


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : Hendri Budi K.

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.