ANALISA MULTIPLE REPAIR PADA PROSES BRAZING TEMBAGA DENGAN STAINLESS STEEL TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK DI PT. X

ANALYSIS OF MULTIPLE REPAIR IN THE PROCESS OF BRAZING COPPER WITH SYAINLESS STEEL TOWARDS THE MICROSTRUCTURE AND MECHANICAL PROPERTIES IN PT.X

Gemilang Luhung Prihatma (6712040039)


Abstrak

PT. X adalah perusahaan yang bergerak pada pembuatan produk teknologi perpindahan panas. Proses pengerjaan suatu produk di PT. X salah satunya adalah menggunakan proses brazing yang masih mengandalkan tenaga manusia. Yang terkadang ditemukan terjadinya kegagalan pada proses brazing. Penelitian ini dilakukan untuk mengetahui dampak dari dilakukan proses multiple repair pada ketahanan terhadap uji kebocoran, penetrasi filler pada pengujian makro, ukuran butir, dan kekuatan tarik. Pada penelitian ini proses brazing yang digunakan adalah torch brazing. Bahan yang digunakan sebagai base metal adalah tube stainless steel type 304L dengan dimensi 200 mm x 0,7 mm x ? 12mm, disambung dengan tube tembaga Y040 dengan dimensi 200 mm x 1 mm x ? 10 mm dan proses fitting dilakukan open end pada tembaga sehingga didapatkan gap 0,02-0,15 mm. proses brezing menggunakan filler L-AG34Sn. Proses repair yang divariasikan sebanyak 0 kali, 1 kali, 2 kali, dan 3 kali. Pervariasi menggunakan 4 spesimen yang akan dilakukan uji kebocoran, uji metalografi (makro dan mikro) dan full section tensile test. Hasil pengujian menunjukan semua spesimen tidak terjadi kebocoran. Untuk uji makro, semua spesimen uji memiliki penetrasi dalam, akan tetapi terdapat void dibeberapa bagian pada spesimen uji dengan variasi repair sebanyak 1 kali repair, 2 kali repair, 3 kali repair. Pada uji mikro menunjukan perubahan ukuran butir pada base metal tembaga yaitu dari 6,5 menjadi 6,0, akan tetapi ukuran butir tidak terjadi perubahan pada stainless steel. Variasi repair juga tidak menunjukan perbedaan pada kuat tarik spesimen uji, ini dikarenakan kuat tarik rata?rata tidak menunjukan perbedaan yang signifikan.


Abstract

PT. X is a company that active in the manufacture of heat transfer technology. One of the manufacture process of the product in PT. X was using a brazing process that still rely on human power. The process that is still carried out by using human power sometimes failure was found in the brazing process. This study was conducted to determine the impact of multiple repair process on the resistance of leakage testing, penetration filler testing on the macro, grain size, and tensile strength. In this study the brazing process that was used is about the torch brazing. The materials that was used as the base metal is stainless steel tube 304L type with its dimensions 200 mm x 0.7 mm x ? 12 mm, and were connected by using copper tube Y040 with its dimensions 200 mm x 1 mm x ? 10 mm and the fitting process performed open end on copper, so gap from 0.02 to 0.15 mm were reached. The process of Brezing was using filler combination of silver L-AG34Sn. Repair process was varied from 0 times, 1 time, 2 times and 3 times. Each variation used four specimens. In this research, leak test, metallographic test (macro and micro) and mechanical tests using a full section tensile test. The result of test showed that there is no leakage on the all specimens. To test the macro all variations repair on the test specimen obtained on the deep penetration, but there is no filler sticking with stainless steel base metal in some parts of the test specimen with variations repair one up to three times repair. At the micro test showed changes in grain size in the base metal copper is from 6.5 to 6.0, but the changes of the grain size does not effect on the stainless steel. Variations repair also showed that there is no difference in tensile strength test specimen, it is because the average tensile strength showed no difference in tensile strength results are significant.


Detil Peneliti

Dosen Pembimbing 1 :Miftachudin
Dosen Pembimbing 2 : Imam Khoirul Rohmat

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.