PENGARUH PENAMBAHAN ELEKTRODA E7018 DAN FILLER METAL ER70S-6 PADA MATERIAL LOW CARBON STEEL MENGGUNAKAN PROSES PENGELASAN SMAW TERHADAP SIFAT MEKANIK DAN HASIL UJI RADIOGRAFI

THE EFFECT OF ADDITION ELECTRODE E7018 AND FILLER METAL ER70S-6 IN LOW CARBON STEEL MATERIAL BY USING WELDING PROCESS SMAW TOWARD MECHANIC CHARACTERISTIC AND RESULT OF RADIOGRAPHY TEST

Firman Wahyu Pratama (6712040038)


Abstrak

Prosedur pengelasan yang benar dan tepat adalah salah satu cara untuk mendapatkan hasil pengelasan yang berkualitas. Pada kasus dilapangan, sering terjadi pelaksaan pengelasan yang tidak sesuai prosedur yang dapat menimbulkan berubahnya sifat mekanik dan timbulnya cacat yang tidak diinginkan. Salah satunya yaitu menambahkan elektroda dan filler metal untuk mendapatkan deposit las yang tinggi sehingga mempercepat progress dan meminimalisir biaya dan waktu. Penelitian ini membahas pengaruh penambahan elektroda E7018 dan filler metal ER70S-6 pada material low carbon steel menggunakan proses pengelasan SMAW terhadap sifat mekanik dan hasil uji radiografi. Pengelasan akan dilakukan dengan proses pengelasan SMAW posisi 1G. Saat fill pass, akan dilakukan penambahan elektroda E7018 dan filler metal ER70S-6 dengan variasi diameter 2.6mm dan 3.2mm. Untuk mengetahui pengaruh terhadap sifat mekaniknya maka dilakukan uji tarik dan uji tekuk serta dilakukan uji ANOVA untuk mengetahui ada tidaknya pengaruh terhadap nilai uji tarik. Selain itu uji radiografi juga dilakukan untuk mengetahui pengaruh penambahan tersebut terhadap isi las. Penelitian ini membuktikan bahwa penambahan elektroda E7018 dan filler metal ER70S-6 pada hasil uji radiografi sebagian besar dinyatakan ada cacat yang disebabkan faktor lain. Pada pengujian tarik tidak mempengaruhi hasil dari uji tarik yang dinyatakan masuk dalam range requirement material, dan juga hasil uji tekuk yang dinyatakan accepted pada semua spesimen serta dibuktikan dengan uji ANOVA yang menyimpulkan tidak adanya pengaruh signifikan pengaruh jenis dan diameter terhadap nilai ultimate tensile strength.


Abstract

The right and appropriate procedure of welding is a way to get best result in welding. There are some cases often happened where people use inappropriate procedure of welding that could make some changes in mechanics characteristic and unwanted flaws. One of them is addition electrode and filler metal to get high weld deposit in order to hasten the progress and minimize time and cost. This research explained about addition electrode E7018 and filler metal ER70S-6 in low carbon steel material by using welding process SMAW toward mechanics characteristic and result of radiography test. Welding process had done by using welding process SMAW in 1G position. After fill pass, the researcher will increase electrode E7018 and filler metal ER70S-6 with two different diameters, 2.6 mm and 3.2 mm. To know the effect toward mechanics characteristic, the researcher had done tensile test and bending test also ANOVA test to know whether there were effects or not toward tensilel test. Besides, radiography test had done as well to know the effects of that addition toward the weld?s content. This research proves that addition electrode E7018 and filler metal ER70S-6 on result radiography most otherwise discontinuity caused another factor. In tensile test not affect to the result of tensile test which be avowed range requirement material and bending test which be avowed accepted in all specimen also proved by using ANOVA test can be concluded that there are no significant effect, kind effect, and diameter toward value of ultimate tensile strength.


Detil Peneliti

Dosen Pembimbing 1 :Bachtiar
Dosen Pembimbing 2 : Mukhlis

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.