PENGARUH PERUBAHAN PARAMETER SPOT WELDING TERHADAP KEKUATAN GESER DAN STRUKTUR MIKRO PADA FERRITIC STAINLESS STEEL TIPE DIN 1.4003 DI PT. INKA

CHANGE EFFECT SPOT WELDING PARAMETER ON SHEAR STRENGTH AND MICRO STRUCTURE OF FERRITIC STAINLESS STEEL TYPE DIN 1.4003 AT PT. INKA

Robbin Maulana Ahmad (6712040035)


Abstrak

ABSTRAK Masalah yang sering muncul pada resistance spot welding adalah kualitas hasil las atau nugget yang terbentuk. Bentuk nugget akan mempengaruhi kekuatan mekanis dari sambungan las, sehingga perlu untuk mengetahui bagaimana cara memperoleh bentuk nugget dengan kualitas baik. Kualitas las (nugget) tersebut dipengaruhi oleh beberapa faktor seperti kualitas permukaaan logam dan perubahan parameter-parameter yang digunakan. Untuk itu, kontrol terhadap kualitas pengelasan perlu diperhatikan dengan mempelajari bentuk dan ukuran nugget yang dihasilkan dari proses resistance spot welding. Material yang digunakan pada penelitian ini adalah ferritic stainless steel DIN 1.4003 dengan dimensi 160 mm x 40 mm x 2 mm yang akan disambung dengan lap joint. Kuat arus (current) yang digunakan sebesar 8 kA, 9 kA dan 10 kA dengan waktu pengelasan (weld time) sebesar 0.25 second, 0.33 second dan 0.42 second. Metode pengujian yang digunakan adalah shear test dan metallography (makro dan mikro). Hasil dari shear test akan diolah data dengan Metode Taguchi untuk optimalisasi. Hasil dari shear test menunjukkan semakin tinggi nilai current dan weld time kekuatan geser semakin meningkat. Kekuatan geser rata-rata terkecil adalah 8,46 kN dan rata-rata terbesar adalah 18,33 kN. Parameter yang paling optimum dengan Metode Taguchi terhadap hasil shear strength adalah current sebesar 10 kA dan weld time 0.42 second. Pada pengujian makro parameter yang menghasilkan diameter nugget sesuai standar adalah parameter 7,8 dan 9 yaitu sebesar 9 mm, 10 mm dan 10 mm. Struktur mikro yang terbentuk dari semua parameter adalah sama, tidak ada perbedaan. Bentuk struktur mikro yang dihasilkan adalah delta ferrite, dari semua parameter struktur yang terbentuk memiliki ukuran butir yang sama. Pada base metal struktur yang terbentuk adalah delta ferrite dengan ukuran kecil. Daerah HAZ memiliki struktur yang semakin besar apabila semakin dekat dengan weld metal, struktur yang terbentuk adalah dendrite. Ukuran butir pada weld metal sangatlah besar yang berbentuk memanjang (columnar grains). Kata kunci: Resistance spot welding, nugget, lap joint, shear strength, ferritic SS DIN 1.4003


Abstract

ABSTRACT In resistance spot welding process, the problem that often happen is about the quality of the weld and how the nugget are formed. The nugget shape will affect mechanical strength of the weld joint, so it needs to find out how to obtain forms of nuggets with good quality. The quality of welding (nugget) is influenced by several factors such as the quality of the metal surface and parameter change they are used. Therefore, the control of welding quality need to be considered by studying the shape and size of the nuggets produced from the resistance spot welding. The material used in this research is ferritic stainless steel DIN 1.4003 with dimensions of 160 mm x 40 mm x 2 mm which will be connected with the lap joint. Electric current used by this research is 8 kA, 9 kA and 10 kA, the weld time is 0.25 second, 0.33 second and 0.42 second. Methods of testing used is shear test and metallography (macro and micro). The data results of the shear test will be processed with the Taguchi method for optimization. The results of the shear test show that the higher value of electrical current and weld time effect on increasing the shear strength. Minimum average shear strength is 8.46 kN and the maximum average of shear strength is 18.33 kN. The most optimum parameters with the Taguchi method to the results of shear strength is a electrical current with 10 kA and weld time 0.42 second. On testing the macro parameter which produces nugget diameter according to the standard is 7.8 and 9 parameter that is equal to 9 mm, 10 mm and 10 mm. The microstructure formed of all the parameters is the same, no difference. The result of the microstructure form is delta-ferrite, of all the parameters of the structure formed have the same grain size. On the metal base formed structure is delta-ferrite with small size. HAZ regions have a structure that increases if getting close to the weld metal, dendrite structure is formed. The grain size in the weld metal is large elongated shape (columnar grains). Keywords : Resistance spot welding, nugget, lap joint, shear strength, ferritic SS DIN 1.4003


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : Usman Dinata

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.