PENGARUH MULTIPLE REPAIR SAMBUNGAN PENGELASAN PIPA ALUMUNIUM 6061-T6 TERHADAP STRUKTUR MIKRO DAN KETAHANAN PITTING CORROSION

EFFECT OF MULTIPLE REPAIR EXPOSURE WELDING PIPE 6061 - T6 ALUMINUM ON MICRO STRUCTURE AND CORROSION PITTING RESISTANCE

Dimas Arif Argananta (6712040032)


Abstrak

Sambungan pengelasan tidak menutup kemungkinan untuk terjadinya cacat pengelasan. Kesalahan proses pengelasan dapat terjadi karena berbagai factor akan menimbulkan kemungkinan terjadinya defect. Multiple repair welding dapat mengakibatkan berpengaruhya tingkat kekuatan, dan struktur itu sendiri. Penilitian ini bertujuan mengetahui hasil multiple repair terhadap struktur mikro dan hasil laju korosi pitting yang terjadi pada pipa alumunium 60661-T6 dengan material OD 4 inch menggunakan pengelasan GTAW. Hasil laju korosi pada sambungan pengelasan menggunakan proses uji sel tiga elektroda dengan larutann NaCl 3,5%, spesimen A1 tanpa repair sebesar 0.01716 mmpy, A2 repair 1x sebesar 0.0439 mmpy dan specimen A3 repair 2x sebesar 0.049mmpy. Hasil pengujian mikro etsa pengelasan tanpa repair menghasilkan butiran yang kasar. Hasil pengujian mikro etsa pengelasan repai 1x dan 2x menghasilkan butiran yang halus. Semakin banyak repair semakin halus butirannya Kata-kata kunci : Multiple Repair, Defect, Aluminium 6061-T6, GTAW, Pitting corrosion


Abstract

The connection to the welding didn?t close the possibilityfor occurrence of defect at the time of welding. Error in welding prosses can be occurred due to varius factors and possibility ocour a defect. Multiple repair welding can result to influential power levels and the structure it self. This research purpose to understood the result of multiple repair against the microstructure and pitting corrosion rate result which occour in aluminium tube 6061-T6 with out side 4 inch use Gas tungsten arc welding (GTAW) welding. The result of the rate of corrosion on the welding connection using three electrode cell test proses with a solution on Nacl 3.5%, specimen A1 with out repair as big as 0.017116 mmpy, A2 first as big as 0.0439 mmpy and specimen A3 second repair as big as 0.049 mmpy. The result of the test micro etching without welding repair produces rough granules. The test result of a micro etching welding repair first and second produce refined granules the more subtle details getting repair Keyword: multiple repair, defect,GTAW, pitting corrosion, aluminium 6061-T6


Detil Peneliti

Dosen Pembimbing 1 :Bachtiar
Dosen Pembimbing 2 : Zuhri Noor

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.