ANALISA VARIASI INTERPASS DAN PERBANDINGAN ELEKTRODA DISSIMILAR METAL ARC WELDING TEE JOINT PADA MATERIAL A-516 GRADE 70 DENGAN A-240 TYPE 316 TERHADAP STRUKTUR MIKRO DAN KETAHANAN KOROSI GALVANIS

ANALYSIS VARIATION INTERPASS AND COMPARISON ELECTRODES DISSIMILAR METAL ARC WELDING THE TEE JOINT IN THE MATERIAL A-516 GRADE 70 WITH A-240 TYPE 316 TO STRUCTURE MICRO AND ENDURANCE CORROSION GALVANIZED

Bagus Prayogo Wibowo (6712040029)


Abstrak

Pada masa sekarang ini banyak sekali ditemukan berbagai macam kasus pengelasan dissimillar metal. Fenomena ini akan menimbulkan penelitian dan pengkajian lebih lanjut tentang penyambungan material yang berbeda agar diperoleh hasil sambungan yang diinginkan tanpa adanya dampak berkelanjutan dari proses pengelasan. Pada supply pressure vessel di PT. Perusahaan Gas Negara (PGN) terdapat permasalahan yang berhubungan dengan pengelasan dissimilar metal yaitu antara stainless steel dan carbon steel menggunakan proses las SMAW. Dalam kasus ini supply pressure vessel yang berbahan dari A-516 grade 70 disambung dengan Mist Extractor yang berbahan dari A-240 TP 316 dimana kedua material tersebut memiliki mechanical properties, chemical composition, dan perlakuan yang berbeda-beda. Maka perlu dilakukan analisa yang mendalam menggunakan variasi elektroda E309, dan E309Mo, untuk mencapai kualitas sambungan yang baik, terutama ditinjau dari ketahanan korosi galvanis, dan struktur mikro dari material yang berbeda tersebut. Pada penelitian ini dilakukan 3 variasi interpass dengan menggunakan elektroda E309 dan E309Mo. Kemudian dilakukan pengujian polarisasi linier berdasarkan standart ASTM G5, pengambilan foto mikro, pengambilan fot dengan menggunakan SEM dan EDX. Hasil penelitian ini menjelaskan bahwa semakin tinggi interpass temperatur mengakibatkan kenaikan laju korosinya, dan penambahan unsur Molybdenum terbukti mampu memberikan efek yang signifikan terhadap ketahanan korosi terutama untuk meningkatkan ketahanan dari serangan korosi sumuran dan celah.


Abstract

On this modern inordinate found various kinds of welding dissimillar the case of metal. This phenomenon will cause research and further analysis about connect different material that the results connection desired without any sustainable impacts of the process welding. In supply pressure vessel in PT. Perusahaan Gas Negara ( PGN ) there is a problem that deals with welding dissimilar metal that was between stainless steel and carbon steel using a process las smaw. In this case supply pressure vessel who made of a-516 grade 70 with jointed mist an extractor who made of a-240 tp 316 in which the two it having the mechanical properties, chemical composition, and treatment different. We need to analysis deep employing variations electrodes E309 , and E309Mo, to reach the quality of connection good, especially in terms of galvanized, corrosion resistance and microstructure of different materials. This research was conducted in three variations E309 electrodes using interpass and E309Mo. Then do linear polarization testing based on standard ASTM G5, micro photo retrieval, retrieval fot using SEM and EDX. The result of this research explained that the higher interpass temperature resulting in the increase in the rate korosinya , and the addition of the elements molybdenum proven able to give the effect of a significant from endurance for corrosion especially to enhance resistance from attack pitting corrosion and a slit.


Detil Peneliti

Dosen Pembimbing 1 :Bachtiar
Dosen Pembimbing 2 : Zuhri Noor

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.