ANALISA PENGARUH JENIS FILLER METAL TERHADAP KETAHANAN PITTING CORROSION PADA PENGELASAN MATERIAL AUSTENITIC STAINLESS STEEL TIPE 316 DENGAN PROSES GTAW

ANALYSIS INFLUENCE KIND OF FILLER METAL TO PITTING CORROSION RESISTANCE IN WELDING AUSTENITIC SYAINLESS STEEL TYPE 316 MATERIAL BY THE GTAW PROCESS

Akhmad Arif Hidayat (6712040025)


Abstrak

ABSTRAK Pada pengelasan GTAW (Gas Tungsten Arc Welding) terdapat dua jenis filler yang digunakan yaitu flux core wire dan solid wire. Pengelasan GTAW yang menggunakan filler solid wire pada proses pengelasannya menggunakan backing gas argon untuk melindungi root dari kontaminasi pada pengelasan pipa stainless steel . Pada pengelasan yang menggunakan filler flux core pada pengelasan pipa stainless steel bagian root dilindungi oleh flux yang terbakar menjadi slag. Dilakukan penelitian bagaimana struktur mikro hasil pengelasan antara flux core wire dan solid wire, serta ketahanannya terhadap korosi pitting. Penelitian filler R 316LT1-5 yang merupakan flux core wire dan filler ER 316L yang merupakan solid wire. Menggunakan material pipa SA 312 tipe 316 dengan diameter dua inch. Pengelasan dilakukan dengan posisi 1G. Penelitian dilakukan dengan mengetahui hasil uji korosi pitting dengan metode sel tiga elektroda dan uji metalografi mikro hasil pengelasan yang menggunakan filler R 316LT1-5 dan filler ER 316L. Untuk pengamatan pitting menggunakan SEM dan EDS. Dari hasil uji metalografi mikro, diketahui bahwa filler R 316LT1-5 dan filler ER 316L memiliki struktur delta ferit dan austenit. Dari hasil pengujian korosi pitting didapatkan nilai laju korosi filler R 316LT1-5 sebesar 0,041 mmpy. Dan nilai laju korosi filler ER 316L sebesar 0,398 mmpy. Dari pengamatan SEM dan analisa EDS kedua variabel filler mengalami korosi pitting diketahui dari unsur yang dominan muncul yaitu Fe, O, dan Cr diperkirakan merupakan produk korosi berupa oksida besi dan oksida krom. Dari semua nilai laju korosi yang diperoleh material tersebut masuk dalam kategori good. Kata kunci : GTAW, flux core wire, solid wire, korosi pitting, sel tiga elektroda, SEM dan EDS


Abstract

ABSTRACT In welding GTAW (Gas Tungsten Arc Welding) there are two types of filler used is flux core wire and solid wire. GTAW welding with solid filler wire welding process using argon backing gas to protect the root of contamination on stainless steel pipe welding. In welding using filler flux core welding stainless steel pipe in the root is protected by flux burned to slag. Do research on how the microstructure of the weld between the flux core wire and solid wire, as well as resistance to pitting corrosion. The research of filler R 316LT1-5 which is a flux core wire and ER 316L filler which is solid wire. Using the pipe material SA 312 type 316 with a two-inch diameter. Welding is done with 1G position. The study was conducted by knowing the pitting corrosion test results with potentiostat linier polarization method and micro metallographic test results using a welding filler and filler 316LT1-5 R ER 316L. For pitting observation using SEM (Scanning Electron Microscopy) and EDS (Energy Dispersive X-ray Spectroscopy). From the micro metallographic test results, it is known that the of filler R 316LT1-5 and ER 316L of filler has a delta ferrite and austenite structure. From the results of pitting corrosion testing corrosion rate values obtained of filler R 316LT1-5 of 0,041 mmpy. And the corrosion rate value ER 316L of filler of 0.398 mmpy. From the observation of SEM and EDS analysis of the two variables of filler known to corrosion pitting of the dominant element emerged, namely Fe, O, and Cr is a product of corrosion in the form of iron oxide and chrome oxide. of all the corrosion rate values obtained material falls within the good category. Keywords : GTAW, flux core wire, solid wire, pitting corrosion, potentiostat linier polarization, SEM and EDS


Detil Peneliti

Dosen Pembimbing 1 :Adhi Setiawan
Dosen Pembimbing 2 : Mukhlis

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.