Analisis Pengelasan Multiple Repair Material SA 240 type 304 Dengan Solution Treatment Terhadap Struktur Mikro Dan Ketahanan Korosi

ANALYSIS MULTIPLE REPAIR TO MICRO STRUCTURE AND CORROSION RESISTANCE OF MATERIAL SA 240 TYPE 304 IN WELDING SMAW WITH SOLUTION TREATMENT 9500 C

Febby Asti Farizal (6712040020)


Abstrak

Kegagalan dalam proses pengelasan stainless steel sering kali terjadi yang mengakibatkan kualitas hasil lasan menurun yang nantinya dapat menimbulkan kegagalan pada suatu produk. Dalam hal ini repair menjadi peranan penting untuk mendukung kualitas hasil lasan. Untuk memperbaiki hasil pengelasan stainless steel yang mengalami repair maka dilakukan perlakuan panas, yaitu solution treatment, Solution treatment dilakukan pemanasan sampai temperatur 950 0C kemudian didinginkan secara cepat menggunakan media air. Dengan perlakuan tersebut dapat mencegah presipitasi karbida yang mengkaibatkan korosi pada batas butir pengelasan Pada penelitian tugas akhir ini menggunakan 3 variasi repair yang berbeda yaitu pengelasan yang tanpa di repair, pengelasan yang di repair 1x, dan pengelasan yang di repair 2x. Pada proses pengelasan menggunakan pengelasan SMAW. Proses pengelasan ini dilakukan dengan beberapa prosedur pengelasan dan pengujian. Untuk material yang digunakan menggunakan material SA 240 type 304. Setelah proses pengelasan selesai dilakukan beberapa pengujian yaitu struktur mikro dan uji sel tiga elektroda. Hasil struktur mikro, terlihat bahwa semakin banyak proses multiple repair welding yang dilakukan, terlihat semakin banyak karbida krom yang terbentuk. Hasil uji sel tiga elektroda didapatkan hasil bahwa laju korosi terendah terdapat pada spesimen A yang tanpa repair yaitu sebesar 0,038753 mmpy, dan tertinggi terdapat pada spesimen C yang di repair 2x yaitu sebesar 0,097693 mmpy. Dapat disimpulkan bahwa material yang semakin banyak di repair semakin tinggi pula nilai laju korosinya. Kata kunci: multiple repair welding, austenitic stainlees steel, SA 240 type 304, pengelasan


Abstract

The failure of stainless stell process welding that often consequence the quality of weld result is go down than can consequence product result failure. In this matter repair become the important role to advocate the quality of result. To repair the result of stainless stell welding that repair so must do heat treatment, this is solution treatment. Solution treatment do with calefaction until 9500C than raipid coling by water media. With this treatment can restrain carbida presipitasi that can make corrosion at the limit of grain size welding. At the research of this last assignment used by 3 different variation repair, that is welding without repair, welding by 1x repair and welding by 2x repair. At the welding process used by SMAW welding. This welding process do by many welding and testing procedures. For material that do by SA 240 type 3014 material. After that welding process done, do many testing that is micro structure and test of potensiostate. The result of micro structure, had seen that more and more the multiple repair welding processes was doing, so there are seen more and more carbida crom. The test result of three matter elektroda gotten that speed of lowest corrosion at the specimen A that without repair, that is 0,038753 mmppy, and highest at the specimen c that by 2 time repair that is 0,097693 mmpy. So, the conclusion is more andmore materials that do repair so more and more high the speed value of corrosion. Keyword: multiple repair welding, austenitic stainlees steel, SA 312 type 304L, pengelasan GTAW dan SMAW


Detil Peneliti

Dosen Pembimbing 1 :Usman Dinata
Dosen Pembimbing 2 : Hendri Budi K.

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.