ANALISA PROSES PENGELASAN 3G VERTICAL UP DAN VERTICAL DOWN PADA LAYER BUILT UP TERHADAP SIFAT MEKANIK DAN STRUKTURE MIKRO, MAKRO.

ANALYSIS OF WELDING PROCESS WITH 3G VERTICAL UP DAN VERTICAL DOWN AT THE BUILT UP LAYER TOWARD MECHANIC CHARACTERISIC AND MACRO MICRO STRUCTURE

Muhammad Arif Rahman Ilmiyahwan (6712040016)


Abstrak

ABSTRAK ANALISA PROSES PENGELASAN 3G VERTICAL UP DAN VERTICAL DOWN PADA LAYER BUILT UP TERHADAP SIFAT MEKANIK DAN STRUKTURE MIKRO, MAKRO. NAMA : MUHAMMAD ARIF RAHMAN ILMIYAHWAN NRP : 6712040016 Pengelasan adalah sebuah proses penyambungan dua atau lebih logam yang banyak di aplikasikan dalam dunia konstruksi dan struktural, ada pun kendala yang sering di alami pada penyambungan logam antara lain gap yang terlalu besar, dengan adanya gap yang terlalu besar ini bisa mempersulit proses penyambungan logam. di AWS D 1.1 sudah mencantumkan beberapa metode atau cara untuk menanggulangi masalah tersebut salah satunya adalah dengan metode built up, penelitian kali ini untuk mengetahui pengaruh proses pengelasan 3G vertical up dan vertical down pada layer Built up. Pada penelitian ini dilakukan 3 variasi Built up dan 2 perbandingan posisi pengelasan pada proses penyambungan diantaranya 1 layer Buit up dengan posisi pengelasan 3G vertical up dan vertical down, 2 layer Built up dengan posisi 3G vertical up dan vertical down, dan 3 layer built up dengan posisi pengelasan 3G vertical up dan vertical down. Kemudian di lakukan pengambilan pengujian sifat mekanik dan struktur mikro, makro berdasarkan standart AWS D 1.1. Hasil penelitian ini menjelaskan bahwa dengan di lakukannya metode Built up mengakibatkan terjadinya kenaikan kekerasan dan perubahan struktur pada logam induk. Penelitian ini nantinya bisa menjadi masukan atau perbandingan pada standart AWS D 1.1. Kata kunci : carbon steel A 36, metode Built up, posisi pengelasan 3G Vertical up dan Vertical down, sifat mekanik, strukture mikro, makro.


Abstract

Welding is a process to joining metal that much be aplicated in contruction and structural work. In welding process there are many problems that often meet when interlock metal, like a biger GAP. GAP that have biger size can make complicated in joining metal process. At AWS D 1.1 included many method to give solution in that problem, one of the method is with built up method. I do the research to know the influence of 3D vertical up and vertical down welding process at the built up layer. In my research used by 3 built up variation and 2 comparison welding position. At interlock process 1 built up layer with 3G vertical up and vertical down welding position, 2 built up layer with 3G vertical up and vertical down welding position and 3 built up layer with 3G vertical up and vertical down welding position. Than take testing mechanic characteristic and micro structure, this macro building on AWS D 1.1 standart. The result of this research is explain that with used built up method can consequence increase violence and change of prominent metal structure. This research can became material of comparison in AWS D 1.1 standart. Keyword : carbon steel A 36, Built up method, 3G vertical up and vertical down welding position, mechanic characteristic, micro structure, macro.


Detil Peneliti

Dosen Pembimbing 1 :Usman Dinata
Dosen Pembimbing 2 : M.Syaiful Amri

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2012


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.