ANALISIS PENGARUH VARIASI WIRE FEED DAN VARIASI KUAT ARUS PADA PENGELASAN ALUMINIUM TERHADAP KETAHANAN GESER DENGAN MENGGUNAKAN METODE SLOT WELDING

ANALYSIS OF THE EFFECT OF WIRE FEED AND WELDING CURRENT VARIATIONS IN THE ALUMINIUM WELDING AGAINST SHEAR RESISTANCE USING SLOT WELDING

Danang Eko Pramono (6711040050)


Abstrak

ABSTRAK Pengelasan Aluminium merupakan pengelasan yang cukup sulit dilakukan. Hal ini dikarenakan adanya lapisan aluminium karbida yang ulet dan memiliki titik didih yang lebih tinggi yaitu 2060 oC jika dibandingkan dengan logam murninya yang meleleh pada 600 oC. Diperlukan cara dan perlakuan khusus dalam melakukan pengelasan aluminium seperti melakukan pembersihan terlebih dahulu terhadap permukaannya, pengaturan kuat arus dan penggunaan wire feed agar mendapatkan hasil pengelasan yang baik. Pada penelitian ini akan digunakan material aluminium seri 5083 dengan dimensi 200 mm x 30 mm x 3 mm yang akan di las menggunakan mesin las GMAW dengan menggunakan metode slot welding. Paramaeter pengelasan yang digunakan yaitu variasi wire feed dan variasi welding current. Dari hasil penelitian dengan menggunakan metode pengolahan data anova, didapatkan bahwa penggunaan variasi wire feed dan kuat arus memililki pengaruh yang cukup signifikan terhadap nilai beban geser sambungan slot welding. Apabila dilakukan analisa data secara individual hasil shear test yang nilainya paling tinggi adalah dengan menggunakan kuat arus 70 ampere dengan wire feed 9.80 m/min yaitu dengan nilai rata-rata 1132.53 kgf. Apabila hasil ini dibandingkan dengan hasil pengujian makro, maka akan terlihat ketidak konsistenan pada hasil kedua pengujian tersebut. Hal ini disebabkan karena spesimen uji shear dan spesimen uji makro menggunakan spesimen yang berbeda sehingga hasil pengelasan juga berbeda. Kata kunci : Aluminium 5083, slot welding, welding current, wire feed, shear test


Abstract

ABSTRACT Aluminum welding is a kind of welding that quit hard to do. That caused corundum which is torgh and has high melting point that 2060 oC than it?s pure metal that melted at 660 oC. special treatment needed in aluminum welding such as cleaning before welding, ampere setting and wire feed viage in orther to peach the best of welding. In this research, the authors will use aluminum material series 5083 with dimension of 200 mm x 30 mm x 3 mm wich will welded by GMAW welding machine wich author will use slot welding method. The variation of welding will be wire feed and welding current. From this result, it was found that the use variation of wire feed and the ammount welding current for slot welding technique in aluminum material, by anova method analysis have a significant impact in the slot weld?s shear resistance. Analysis data in individual way, the result of shear test wich has highest result is by using 70 ampere with wire feed 9.80 m/min, that mean 1132.53 kgf. This result is comprehended with macro eatcha test that welding with 70 ampere current and 9.80 wire feed also has biggest penetration valve of 2.45 mm. on the orther hand the result of hardness test the number is 57.453 BHN as the highest hardness which in welding with 70 ampere current and 9.80 m/min wire feed. Key word: Aluminum 5083, slot welding, welding current, wire feed, shear test


Detil Peneliti

Dosen Pembimbing 1 :Bachtiar
Dosen Pembimbing 2 : Hendri Budi K.

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.