PENGARUH JENIS FILLER METAL PADA PENGELASAN MATERIAL SUS 316 L PADA LINE HP FEED WATER TERHADAP KETAHANAN KOROSI DAN KEKERASAN

THE EFFECT WELDING OF METAL FILLER ON MATERIAL SUS 316L AGAINST HP FEED, WATER LINE AGAINST CORROSION RESISTANCE AND HARDNESS

Mochammad Rizky Maulidin (6711040042)


Abstrak

Boiler (ketel uap) berfungsi untuk menghasilkan uap fase panas untuk memutar turbin. Dengan berputarnya turbin maka poros turbin generator yang merupakan seporos dengan turbin otomatis akan ikut berputar. Dari generator inilah listrik dapat dihasilkan, adapun sisa uap pada turbin akan dikondensasikan di condenser untuk dimanfaatkan lagi. Pada penelitian ini bertujuan untuk mengetahui apakah dengan selisih kandungan Chromium yang signifikan pada Filler Metal 316L dan Filller Metal 309L yang di sambung dengan pipa tipe SS 316L dengan variasi kuat arus sebesar 60A, 70A, serta 80A bisa mempengaruhi mechanical properties, serta apakah dari segi hasil pengujian laju korosi dan kehilangan massanya akan ikut signifikan juga. Berdasarkan pengujian yang telah dilakukan diketahui bahwa unsur Cr pada filler metal A1 (316L) dan A2 (309L) berpengaruh pada pengujian hardness dan laju korosi, yaitu pada pengujian hardness nilai kekerasan rata ? rata yang paling tinggi ada pada filler metal A2 (309L) dengan ampere 80 pada daerah HAZ, sedangkan nilai kekerasan yang cenderung lebih rendah ada pada daerah Base Metal secara keseluruhan, dan sedangkan untuk pengujian laju korosi diketahui bahwa filler metal A2 (309L) arusnya lebih besar, potensial korosi dari weld metal dilihat dari ICOR yang lebih besar selisihnya dari base metal, sedangkan kalau dilihat dari ECOR selisihnya sebesar 100 mv, dan untuk filler metal A1 (316L) diketahui bahwa laju korosi pada daerah weld metal ECORnya lebih kecil, akan tetapi ICORnya cenderung lebih besar nilai laju korosinya.


Abstract

Boiler is used to produce steam to turn turbines hot phase . With the rotation of the turbine shaft turbine generator with a turbine which is seporos automatically rotates . From this generator of electricity can be generated , while the rest of the steam in the turbine will be condensed in the condenser to be used again . In this study aims to determine whether the significant difference in the content of Chromium Metal Filler Metal Filller 316L and 309L are in the pipeline continued with variations of type 316L SS with a strong current of 60A , 70A , and 80A can affect the mechanical properties , as well as whether in terms of results testing corrosion rate and significant loss of mass will participate as well . Based on the testing that has been made known that Cr in the filler metal element A1 ( 316L ) and A2 ( 309L ) effect on the testing of hardness and corrosion rate , ie the average hardness value of hardness testing - the average is highest in the filler metal A2 ( 309L ) with 80 ampere at HAZ region , while the hardness values tend to be lower there on metal Base area as a whole , and while testing for corrosion rate is known that the filler metal A2 ( 309L ) current is greater , the potential corrosion of the weld metal seen from the larger ICOR the difference of the base metal , while judging from ECOR difference of 100 mV , and for the filler metal A1 ( 316L ) note that the rate of corrosion of the weld metal ECORnya area is smaller , but tend to be larger ICORnya corrosion rate value


Detil Peneliti

Dosen Pembimbing 1 :Bachtiar
Dosen Pembimbing 2 : Wiwik Dwi Pratiwi

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2011