ANALISIS PENGGUNAAN FILLER METAL TGX 316L SEBAGAI ALTERNATIF PENGGANTI FILLER METAL ER 316L PADA PENGELASAN PIPA STAINLESS STEEL SA 312 TP 316L MENGGUNAKAN PROSES GTAW

ANALYSIS OF FILLER METAL TGX 316L AS FILLER METAL ER 316L SUBSTITUTE IN STAINLESS STEEL PIPE SA 312 TP 316L WELDING USING GTAW PROCESS.

Haris Kurniansyah (6711040040)


Abstrak

Baja tahan karat jenis austenitik tipe SA 312 TP 316L banyak digunakan di berbagai Industri, salah satunya yaitu digunakan untuk flare stack pada proyek ?Banyu Urip?. Untuk menyambungkan antar pipa dilakukan proses pengelasan, salah satu proses pengelasan yang sering dilakukan adalah GTAW (Gas Tungsten Arc Welding), dimana untuk pengelasan stainless steel menggunakan proses GTAW membutuhkan purging gas sebagai pelindung dari kontaminasi udara luar. Namun penggunaan purging gas sebagai pelindung menimbulkan adanya penambahan biaya yang cukup besar apalagi jika proses pengelasan dilakukan pada material dengan dimensi yang besar. Pada penelitian ini akan dilakukan pengelasan pada pipa stainless steel 4? sch 40 dengan variasi penggunaan filler metal ER 316L dan filler metal TGX 316L. Setelah proses pengelasan maka akan dilakukan beberapa pengujian seperti pengujian tarik dan bending sebagai syarat utama pembuatan WPS, pengujian metalografi untuk melihat struktur mikro yang terjadi pada daerah yang menggunaan filler TGX 316L dan filler ER 316L dan juga untuk mengetahui besarnya kekerasan yang terjadi dilakukan pengujian hardness. Diharapkan penggunaan filler TGX dapat menghasilkan sifat mekanik, struktur mikro dan hasil kekerasan yang sebaik bahkan lebih baik dari penggunaan filler ER 316L sehingga dengan biaya produksi yang lebih murah didapatkan kualitas yang sama bahkan lebih baik. Hasil penelitian menunjukan bahwa sifat mekanik yang dihasilkan tidak terpengaruh oleh penggunaan filler metal sedangkan dari struktur mikro yang dihasilkan, daerah filler TGX mempunyai struktur yang lebih halus baik pada daerah HAZ maupun daerah root, hal ini karena adanya flux core yang meleleh membentuk lapisan silica (slag) yang dapat mengontrol cooling rate sehingga panas merambat perlahan bahkan ke samping ke arah HAZ dan menyebabkan daerah HAZ mempunyai butiran yang lebih halus dan lebih ductile daripada HAZ pada filler ER 316L. Kata kunci : Filler TGX 316 L, Filler ER 316 L, pengelasan GTAW


Abstract

ABSTRACT Austenitic stainless steel type SA 312 TP 316L is widely used in various industries,for example is flare stack in ?Banyu Urip? project. Pipe is connected by welding, one of the welding process that often be use is GTAW (Gas Tungsten Arc Welding), welding for stainless steel using GTAW process requires purging gas as a protection from the outside air contamination. However, the use of gas purging as a protective pose need any additional significant costs, especially if the welding process is performed on material with large dimensions. This research will be carried out welding on stainless steel pipe 4 "sch 40 with a variation of the use of filler metal is that ER 316 L and filler metal TGX 316 L. After the welding process is done will be performed several tests such as tensile and bending tests as main requirement to make WPS, testing metallographic to see the microstructure in the area which uses filler TGX 316L and filler ER 316L, and then to know the level of violence use hardness testing. expected that using filler TGX can produce mechanical properties, microstructure and hardness results are as good as or even better than the use of filler ER 316L, so with cheaper production costs obtained the same quality even better. The results of research showed that the mechanical properties generated are less affected by the use of a filler metal while the resulting microstructure, TGX filler area has a finer structure both on regional and local HAZ root, this is because of the flux core that melts to form a layer of silica ( slag ) which can control the cooling rate so that the heat propagates slowly sideways and causing HAZ region so has a finer grain and more ductile than the HAZ on ER 316L. Keywords: Filler TGX 316 L, Filler ER 316 L, GTAW welding


Detil Peneliti

Dosen Pembimbing 1 :Soeweify
Dosen Pembimbing 2 : Moh. Miftachul Munir

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.