PERBANDINGAN PENGARUH ELEKTRODA E309MOL-17 DENGAN ENiCrFe-2 TERHADAP STRUKTUR MIKRO, KEKERASAN DAN LAJU KOROSI PADA SAMBUNGAN ANTARA MATERIAL SA-240 TP 304 DAN SA-387 GRADE 22 PADA PROYEK INLET DAN EXHAUST SISTEM UNTUK IRAQ DAN ARGENTINA DI PT. SWADAYA GR

INFLUENCE THE COMPARISON OF ELECTRODE E309MoL-17 WITH ENiCrFe-2 TO STRUCTURE OF MICRO, HARDNESS AND CORROSION RATE OF MATERIAL CONNECTION BETWEEN SA-240 TP 304 AND SA-387 GRADE 22 PROJECT INLET AND EXHAUST SYSTEM FOR IRAQ AND ARGENTINA IN PT. SWADAYA GRA

Devan Aprian Pradikas Mukti (6711040036)


Abstrak

PT. Swadaya Graha merupakan perusahaan yang bergerak dibidang fabrikasi dan konstruksi mendapatkan pekerjaan berupa fabrikasi 8 unit inlet dan exhaust system untuk proyek duhoq iraq dan fabrikasi 2 unit inlet dan exhaust system untuk argentina. Dimana owner dari kedua proyek tersebut adalah PT. BALTEC dari australia. Pada fabrikasi inlet dan exhaust system tersebut terdapat proses pengelasan yang melibatkan yang melibatkan 2 material yang berbeda yaitu material SA-240 TP 304 dan material SA-387 Grade 22 yang dilas menggunakan proses las SMAW dengan elektroda ENiCrFe-2. Tetapi penggunaan elektroda ENiCrFe-2 dianggap terlalu mahal baik dari segi harga atau dari segi pengerjaan, padahal disisi lain elektroda E309MoL-17 dapat juga digunakan sebagai alternatife karena harganya jauh lebih murah yaitu satuperempat kali dari harga elektroda ENiCrFe-2 dan juga murah dalam pengerjaannya. Dalam penelitian ini dilakukan 2 variabel, yaitu pengelasan dengan elektroda E309MoL-17 dan pengelasan dengan elektroda ENiCrFe-2. Material yang digunakan untuk penelitian ini adalah SA 240 TP 304 dan SA 387 Gr 22. Proses las yang digunakan adalah SMAW, sedangkan untuk pengelasannya sesuai dengan welding procedur specification (WPS) yang sudah dibuat sebelumnya di PT. Swadaya Graha. Hasil pengelasan menggunakan welding procedur specification (WPS) E309MoL-17 dan ENiCrFe-2 acceptable berdasarkan hasil uji radiografi. Dari hasil uji struktur mikro didaerah HAZ SA 387 Gr 22 menunjukkan bahwa penggunaan elektroda E309MoL-17 dan ENiCrFe-2 terbentuk Ferrite dan pearlite sedangkan didaerah HAZ SA 240 TP 304 dengan elektroda E309MoL-17 terbentuk austenit dan elektroda ENiCrFe-2 terbentuk chromium carbide. Dari hasil pengujian kekerasan menunjukkan bahwa dengan elektroda ENiCrFe-2 rata-rata kekerasan yang dihasilkan lebih rendah, tetapi penurunan kekerasan tidak lebih dari 5% dibandingkan penggunaan elektroda E309MoL-17. Dan dari uji laju korosi elektroda E309MoL-17 lebih rendah laju korosinya pada media korosi NaCl 3,5%. Kata kunci : E309MoL-17, ENiCrFe-2, Microstructure, Hardness, Corrosion rate


Abstract

PT. Swadaya Graha is a company enganged in the fabrication and construction of getting a job in the form of 8 units fabricated inlet and exhaust system for the project duhoq Iraq and fabrication of 2 units of inlet and exhaust system for argentina. Where the owner of the project are PT. BALTEC of Australia. In the fabrication of inlet and exhaust system are welding processes that involve involving two different materials, namely a material SA-387 Grade 22 and material SA-240 TP 304 are welded using SMAW welding process with ENiCrFe-2 electrode. But the use of electrode ENiCrFe-2 is considered too costly both in term of price or in terms of workmanship, whereas the other side electrode E309MoL-17 can also be used as alternatives because the price is much cheaper that satuperempat times the price of electrodes ENiCrFe-2 and also low in the process. In this research use two variables, namely welding E309MoL-17 electrode and welding with ENiCrFe-2 electrode. The material used for this research is SA-240 TP 304 ans SA-387 Gr 22. Process SMAW welding is used, while for welding according to the welding procedure of specification (WPS) that was made earlier in the PT. Swadaya Graha. Result welding using a welding procedure of specification (WPS) E309MoL-17 and ENiCrFe-2 acceptable based on the result of radiographic test. From the test result HAZ micro structure area SA-387 Gr 22 show that the use electrodes E309MoL-17 and ENiCrFe-2 formed ferrite and pearlite area while HAZ SA-240 TP 304 with E309MoL-17electrode form austenite and with ENiCrFe-2 electrode form of chromium carbide. Form the result indicate that the electrode hardness ENiCrFe-2 average produced lower hardness, but a decrease in hardness is not more than 5% compared to the use of electrodes E309MoL-17. And the corrosion rate of the test electrode E309MoL-17 lower the rate of corrosion in 3,5% NaCl corrosive media. Keyword: E309MoL-17, ENiCrFe-2, Microstrucutre, Hardness, Corrosion rate


Detil Peneliti

Dosen Pembimbing 1 :Moh. Miftachul Munir
Dosen Pembimbing 2 : Hendri Budi K.

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.