PENGARUH KUAT ARUS DAN KOMPOSISI GAS PELINDUNG ARGON ? CO2 PADA PENGELASAN FCAW TERHADAP SIFAT MEKANIK MATERIAL SA 36

THE INFLUENCE OF CURRENT AND ARGON SHIELDING GAS COMPOSITION - CO2 ON FCAW WELDING ON MECHANICAL PROPERTIES OF MATERIALS SA 36

Aldri Alan Krisdiantoro (6711040034)


Abstrak

FCAW adalah pengelasan busur listrik fluks inti tengah / pelindung inti tengah. Salah satu jenis las listrik yang memasok elektrodasecara mekanis terus kedalam busur listrik yang terbentuk diantara ujung elektroda dan logam induk. FCAW menggunakanelektroda dimana terdapat serbuk fluks di dalam batangnya. Oleh karena itu, penggunaan kuat arus dan gas pelindung sangat diperhatikan untuk mendapatkan hasil pengelasan yang baik. Pada penelitian ini akan menggunakan material SA 36, yang dilas FCAW menggunakan elektroda E71T dengan variasi tiga kuat arus yaitu 100A, 120A dan 140A, serta tiga variasi jenis gas pelindung yaitu C02, Argon, dan campuran C02 Argon. Pengujian yang akan dilakukan adalah uji tarik, uji kekerasan dan uji lengkung. Dari hasil penelitian, didapatkan bahwa peningkatan kuat arus dan penggunaan campuran gas pelindung dapat meningkatkan sifat mekanik pada material SA 36 secara signifikan pada metode uji ANOVA. Ini dapat dibuktikan pada spesimen variasi kuat arus 100A dan gas pelindung CO2 mempunyai nilai rata-rata hasil uji kuat tarik terendah, yaitu 493.35 MPa, sedangkan untukvariasi kuat arus 140A dan gas pelindung CO2 Argonmempunyai nilai rata-rata hasil uji kuat tarik tertinggi, yaitu 519.76 Mpa, serta pada spesimen variasi kuat arus 100A dan dengan gas pelindung CO2 mempunyai nilai rata-rata hasil uji kekerasan terendah, yaitu 177.94 HVN pada weld metal, dan 151.7 HVN pada HAZ, sedangkan untuk variasi kuat arus 140A dan dengan gas pelindung CO2 Argon mempunyai nilai rata-rata hasil uji kekerasan tertinggi, yaitu 184.73 HVN pada weld metal, dan 157.06 HVN. Kata kunci : FCAW, gas pelindung, ampere, A36 , ANOVA


Abstract

FCAW is electric arc welding flux core middle / central core protector. One type of electric welding electrode that supplies mechanically continue into the electric arc formed between the electrode tip and the base metal. FCAW uses electrodes where there is a flux powder inside the trunk. Therefore,the use of strong currents and protective gas is of considerable concern to obtain good welding results. This research will use the material SA 36, were welded using the FCAW electrode E71T with three variations of strong currents, namely 100A, 120A and 140A, and three variations of the type of protective gas is C02, Argon,and a mixture of C02 Argon. Tests will be done is tensile test, hardness test and bend tests. From the research, it was found that the strong increase in the flow and use of protective gas mixture can improve the mechanical properties of the material significantly SA 36 ANOVA test methods.This can be evidenced in the strong current variations specimen 100A and CO2 shielding gas has an average value of tensile strength test results lowest at 493.35 MPa, while for strong variation 140A currents and CO2 Argon shielding gas has an average value of the results of the highest tensile strength test , namely 519.76 Mpa,as well as the current strong variation specimen 100A and with CO2 shielding gas has an average value of test results of low hardness, ie 177.94 HVN in the weld metal, and 151.7 HVN in the HAZ, while for strong variation of flow 140A and the CO2 Argon shielding gas has a value Average highest hardness test results, namely 184.73 HVN in the weld metal, and 157.06 HVN Keywords: FCAW, shielding gas, ampere, A36, ANOVA.


Detil Peneliti

Dosen Pembimbing 1 :Bachtiar
Dosen Pembimbing 2 : Hendri Budi K.

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.