PENGARUH PROSES CHEMICAL CLEANING PADA MATERIAL ALUMINIUM 5083 TERHADAP HASIL PENGUJIAN RADIOGRAFI DAN SIFAT MEKANIK

EFFECT OF CHEMICAL PROCESS CLEANING OF THE MATERIAL ALUMINIUM 5083 Radiography TEST RESULTS AND MECHANICAL PROPERTIES

Alfian Rahadi Putra (6711040030)


Abstrak

ABSTRAK Aluminium 5083 merupakan material paduan unsur Al (aluminium) dan unsur magnesium (Mg) yang pembuatannya dengan cara strain hardening sehingga menciptakan material aluminium yang anti korosi serta memiliki kekuatan yang baik. Pengelasan aluminium memiliki permasalahan antara lain yaitu lapisan pasifnya (Al2O3) dimana apabila senyawa ini bereaksi dengan uap air akan menjadiHydrated alumina saat aluminium terpapar dalam udara bebas pada waktu tertentu dan akan menimbulkan porosity apabila dilakukan pengelasan. Dalam kasus ini, dicari metode yang tepat supaya hasil kualitas pengelasan yang baik pada material. Dilakukan sebuah penelitian, dengan 2 variasi pembersihan dan 2 metode pembersihan. Variasi dan metode pembersihan antara lain menggunakan penggerindaan dan dicelupkan, dikuas pada larutan kimia NaOH 10% dengan dipanaskan sampai temperatur 70? C selama 45 detik kemudian dibasuh dengan air Nitrat Absolut 15% selama 2 menit kemudian dicuci dengan air dingin dan air panas lalu dikeringkan, variasi dan metode yang kedua dengan larutan kimia H3PO4 10%. Hasilnya adalah pembersihan yang paling baik dengan menggunakan pembersihan NaOH 10% (70?C) NaNO3 15% dengan hasil porositas yang lebih sedikit dibandingkan dengan menggunakan pembersihan H3PO4 10% (70?C) NaNO3 15% dan metode pembersihannya dengan dikuas karena lebih efisien dan menghemat cairan kimia.


Abstract

ABSTRACT Aluminium 5083 is a material alloy element of Al (aluminum) and the element magnesium (Mg), whose creation by means of strain hardening thus creating anti-corrosive aluminum material and has good strength. Welding aluminum has a problem, among others, a passive layer (Al2O3) which if the compound is reacted with water vapor to be menjadiHydrated alumina aluminum when exposed to free air at a certain time and will cause porosity when welding done. In this case, look for the appropriate method that results in good welding quality material. Carried out a study, with two variations of cleaning and 2 cleaning methods. Variations and cleaning methods include the use of grinding and dipped, dikuas the chemical solution with 10% NaOH heated to a temperature of 70 ? C for 45 seconds and then washed with water Nitrate Absolut 15% for 2 minutes then washed with cold water and hot water and then dried , variations and methods are second with 10% H3PO4 chemical solution. The result is the best cleaning using the cleaning of NaOH 10% (70 ? C) NaNO3 15% with less porosity results compared to using cleaning H3PO4 10% (70 ? C) NaNO3 15% and the cleaning method with dikuas for more efficient and saves liquid chemicals.


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : Muhamad Ari

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.