ANALISIS PENGARUH INTERPASS TEMPERATURE DAN CHEMICAL SURFACE TREATMENT TERHADAP KETAHANAN SERANGAN PITTING CORROSION PADA MATERIAL SA 240 TYPE 304

ANALYSIS OF THE INFLUENCE OF INTERPASS TEMPERATURE AND CHEMICAL SURFACE TREATMENT TO PITTING CORROSION ATTACK RESISTANCE ON SA 240 TYPE 304

Ricky Angga Alfian (6711040028)


Abstrak

Saat ini banyak industri yang menggunakan austenitic stainless steel (SA 240 Type 304) sebagai bahan pembuatan tangki karena baja jenis ini memiliki ketahanan korosi. Dalam pengelasannya, pengaturan heat input sangat penting karena dapat mempengaruhi pembentukan oxide scale sehingga penggunaan interpass temperature harus tepat. Pembentukan oxide scale ini dapat mempengaruhi ketahanan serangan pitting corrosion maka diperlukan chemical surface treatment untuk menghilangkan oxide scale. Pada penelitian ini terdapat 2 variabel yaitu interpass temperature yang menggunakan ambient temperature dan 1500C, dan chemical surface treatment yang menggunakan HNO3 pekat, HCl pekat, dan H2SO4 pekat. Selanjutnya dilakukan pengujian pitting corrosion berdasarkan standard ASTM G 48 dan evaluasi pitting berdasarkan ASTM G 46 meliputi densitas, ukuran, kedalaman, dan bentuk pitting. Berdasarkan hasil penelitian ini ditemukan bahwa penggunaan interpass temperature dengan ambient temperature dan chemical surface treatment HNO3 pekat memberikan hasil yang lebih baik jika dibandingkan dengan variasi yang lain. Dari hasil evaluasi pitting untuk densitas, ukuran, dan kedalaman terdapat perbedaan nilai tetapi masih dalam rating yang sama, sedangan untuk bentuk setiap spesimen memiliki bentuk yang bervariasi tetapi bentuk subsurface banyak ditemukan. Kata kunci : austenitic stainless steel, oxide scale, pitting corrosion, interpass temperature, chemical surface treatment


Abstract

In these day many industries that use austenitic stainless steel (SA 240 type 304) as material to make the tank because this material have corrosion resistance. In the welding, setting heat input is very important because it can affect the formation of oxide scale so that the use of interpass temperature must be right. The formation of oxide scale can affect pitting corrosion attack resistance so that needed chemical surface treatment to remove oxide scale. In this study, there are two variables that interpass temperature using ambient temperature and 1500C, and chemical surface treatment using concentrated HNO3, concentrated HCl and concentrated H2SO4. Then, pitting corrosion testing performed by ASTM G 48 and evaluation of pitting corrosion performed by ASTM G 46 which include density, size, depth and shape of pits. Based on the result of this study explained that the use interpass temperature with ambient temperature and chemical surface treatment with concentrated HNO3 give better result than the other variation. From the result of evaluation, density, size, depth are different values, but still within the same rating, while for the shape of each specimen has a variation shape, but subsurface shape more found than the others . Key word : austenitic stainless steel, oxide scale, pitting corrosion, interpass temperature, chemical surface treatment


Detil Peneliti

Dosen Pembimbing 1 :Wiwik Dwi Pratiwi
Dosen Pembimbing 2 : Moh. Miftachul Munir

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.