PENGARUH TIG DRESSING TERHADAP FATIGUE STRENGTH SAMBUNGAN LAS SA 516 Gr 70 UNTUK LIQUID KNOCK OUT DRUM

TIG DRESSING EFFECT ON FATIGUE STRENGTH WELD JOINT SA GR 516 70 FOR LIQUID DRUM KNOCK OUT Authors: Ergine de robby Ferdinand panjaitan NRP. 6711040020 Lecture: Ir. Soewefy, M., Eng NIP. 196808301997021001 Mohammed Ari, ST., M.Sc NIP. 196008031988031004

Ergine De Robby Ferdinan Panjaitan (6711040020)


Abstrak

Dewasa ini perlakuan terhadap pengelasan sangat diperhatikan. Mulai dari awal hingga akhir proses pengelasan begitu diperhatikan untuk menghasilkan nilai kualitas pengelasan yang diinginkan. Dalam proses pengerjaan Liquid Knock Out Drum ini ada beberapa bagian yang di kerjakan dengan proses pengelasan GTAW dan SMAW pada filling dan capping nya. Dari beberapa hasil proses pengelasan SMAW pada sambungan shell dan head di temukan sudut pada daerah weld toe kecil. Jika di bagian weld toe tersebut memiliki sudut yang kecil, maka konsentrasi tegangan akan meningkat, hal ini yang menyebabkan weld metal dapat terjadi defect berupa crack. Sudut pada daerah Weld toe dapat diperlebar dengan cara menggunakan metode TIG dressing. Metode TIG dressing bertujuan untuk memperlebar sudut weld toe, agar nilai konsentrasi tegangan menurun. Salah satu cara untuk memprediksi fatigue life dapat menggunakan ANSYS. Kata-kata kunci : TIG dressing, konsentrasi tegangan, fatigue, mean stress, radiograph test, ansys


Abstract

TIG DRESSING EFFECT ON FATIGUE STRENGTH WELD JOINT SA GR 516 70 FOR LIQUID DRUM KNOCK OUT Authors: Ergine de robby Ferdinand panjaitan NRP. 6711040020 Lecture: Ir. Soewefy, M., Eng NIP. 196808301997021001 Mohammed Ari, ST., M.Sc NIP. 196008031988031004 ABSTRACT Today the treatment of the weld are concerned. Starting from the beginning to the end of the welding process so considered to produce the desired value of welding quality. In the process of Liquid Knock Out Drum there are some parts that was done with GTAW and SMAW welding process at its filling and capping. From some of the SMAW welding process results in connection shell and head were found in the area of the weld toe angle is small. If at the weld toe has a small angle, the stress concentration will increase, it is that causes the metal weld defects can occur in the form of crack. Weld toe angle of the area can be enlarged by using the methods TIG dressing. TIG dressing method aims to widen the weld toe angle, so that the value of the stress concentration decreases. One way to predict the fatigue life can use ANSYS. Key words: TIG dressing, stress concentration, fatigue, mean stress, radiograph test, ANSYS


Detil Peneliti

Dosen Pembimbing 1 :Soeweify
Dosen Pembimbing 2 : Muhamad Ari

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.