ANALISA PERBANDINGAN BUTTERING PADA SISI CARBON STEEL DENGAN PENGISI E8018 DAN BUTTERING PADA SISI STAINLESS STEEL DENGAN PENGISI E309 TERHADAP SIFAT MEKANIK DAN KOROSI SAMBUNGAN DISSIMILAR SA-516 GR 70 DAN SA 240 TP 304

BUTTERING COMPARATIVE ANALYSIS ON THE CARBON STEEL WITH ELECTRODE BUTTERING E 8018 AND ON THE STAINLESS STEEL WITH ELECTRODE E 309 TO MECHANICAL PROPERTIES AND CORROSION OF JOINING DISSIMILAR SA 516 AND SA 240 TP 304.

Dedik Iskandar (6711040018)


Abstrak

ABSTRAK ANALISA PERBBANDINGAN BUTTERING PADA SISI CARBON STEEL DENGAN LOGAM PENGISI E 8018 DAN BUTTERING PADA SISI STAINLESS STEEL DENGAN LOGAM PENGISI E 309 TERHADAP SIFAT MEKANIK DAN KOROSI SAMBUNGAN DISSIMILAR SA-516 Gr.70 DAN SA-240 TP 304 Oleh: Dedik Iskandar NRP: 6711040018 Dalam proses fabrikasi support pressure vessel dissimilar sering terjadi tidak sesuainya dimensi material akibat kesalahan pemotongan atau alasan yang lainnya. Saat dimulainya proses pengelasan, dimensi plat yang salah potong tersebut akan berdampak pada gap yang terlalu lebar. Akibatnya sulit untuk dilakukan proses pengelasan untuk menyambung material tersebut dengan material yang lainnya. Dengan metode buttering diharapkan dapat menanggulangi gap yang terlalu lebar. Dalam penelitian ini digunakan variasi buttering carbon steel dengan electrode E 8018, pengisi E 309 dan buttering stainless steel dengan electrode E 309, pengisi E 8018. Hasil uji tarik buttering pada stainless steel lebih baik karena mempunyai nilai rata-rata yield strength sebesar 454,845 mpa, dan nilai rata-rata yield ultimate sebesar 606,475 mpa. Didukung nilai kekerasan pada weld metal 193,942 HVN pada buttering 215,0078 HVN, pada HAZ stainless steel 212,7219 HVN dan HAZ carbon steel 153,1148 HVN. Sedangkan hasil pengujian buttering pada carbon steel dengan electrode E 8018 nilai rata-rata yield strength sebesar 460,42 mpa, dan nilai rata-rata yield ultimate sebesar 616,76 mpa. Untuk hasil dari uji bending kedua spesimen semua dapat diterima. Sedangkan pada hasil dari perhitungan laju korosi yang lebih lambat terdapat pada spesimen dengan proses buttering pada material SA-516 dengan electrode buttering E 8018 yaitu 0,1627 mmpy, sedangkan buttering material stainless steel SA-240 TP 304 dengan electroda buttering E 309 lebih cepat yaitu 0,1859 mmpy. Kata kunci : buttering, carbon steel, stainless steel, dissimilar.


Abstract

ABSTRACT BUTTERING COMPARATIVE ANALYSIS ON THE CARBON STEEL WITH ELECTRODE BUTTERING E 8018 AND ON THE STAINLESS STEEL WITH ELECTRODE E 309 TO MECHENICAL PROPERTIES AND CORROSION OF JOINING DISSIMILAR SA 516 AND SA 240 TP 304. By: Dedik Iskandar NRP : 6711040018 In the process of fabricating support pressure vessel dissimilar often occur does not according with material dimensions result of an error of cutting or reasons other. The commencement of the process of welding , dimensions plate that wrong the cut will have an impact on gap that is too wide. As a result hard to do the process of welding to revive the materials with the material the others. With the methods buttering expected to be able to cope with the gap that is too wide . In this research used variations buttering carbon steel with electrode E 8018, filler e 309 and buttering of stainless steel with electrode E 309, filler E 8018 . Testing shows pull buttering on stainless steel better because it has value the average yield strength 454,845 mpa as much as, and the value of the average yield ultimate 606,475 mpa as much as. Supported the value of violence in weld metal 193,942 hvn on buttering 215,0078 hvn, on haz stainless steel 212,7219 hvn and haz carbon steel 153,1148 hvn. While the results of testing on carbon steel with electrode buttering E 8018 460,42 strength of the value of the average yield of mpa, and the value of the average yield of an ultimate 616,76 mpa. The second Bending to the results of the specimen all accepted. While on the outcome of the calculation of the rate of corrosion that there are more slowly in a specimen buttering with the process in the material SA-516 with electrode buttering e 8018 namely 0,1627 mmpy, buttering the stainless steel materials SA-240 TP 304 with electrode E 309 so faster which 0,1859 mmpy. Key word : Buttering , carbon steel , stainless steel , dissimilar.


Detil Peneliti

Dosen Pembimbing 1 :Usman Dinata
Dosen Pembimbing 2 : Zuhri Noor

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.