Analisa Pengaruh Kuat Arus Dan Teknik Pengelasan Single Pass Dan Multi Pass Multi Layer Pada Posisi 2G Terhadap Sifat Mekanik Dan Struktur Micro

ANALYSIS OF THE EFFECT OF CURRENT STRENGTH AND SINGLE PASS AND MULTIPASS MULTILAYER WELDING TECHNIQUES OF 2G POSITION TO MECHANICAL PROPERTIES AND MICRO STRUCTURE

Muchamad Muhkzinin (6711040009)


Abstrak

PT Barata Indonesia merupakan badan usaha milik negara (BUMN) dimana kegiatan usaha yang dilakukan bergerak di bidang industri argo, industri migas dan industri pembangkit tenaga listrik. Salah satu aplikasi yang dilakukan oleh PT Barata Indonesia saat ini adalah mengembangkan Storage Tank, yang mana Storage Tank ini sangat luas kebutuhan dalam industri MIGAS, untuk itu perlu dilakukan desain dan proses fabrikasi yang tepat. Dalam penelitian ini akan membandingkan pengaruh kuat arus yang berbeda dengan teknik penglasan single pass dan Multipass Multilayer melalui pengujian Radiografi Test, Mikro etsa, Hardness Test dan Impact Test. Kuat arus yang digunakan adalah 75A, 90A, dan Kombinasi (75-90A), proses pengelasan menggunakan mesin las SMAW posisi 2G dan polarity DC ( ), Elektroda yang digunakan semua sama E7018 diameter 2,6 mm. Hasil pengujian dari 6 Spesimen didapat nilai kekerasan yang paling tinggi adalah pada pengelasan Multipass Multilayer di daerah Weld Metal yaitu 215,62 HVN. Sedangkan untuk nilai rata ?rata paling tinggi pada pengujian ketangguhan adalah pada pengelasan dengan teknik single pass Multilayer di daerah Weld Metal yaitu 148,5 J dan nilai ketangguhan yang paling rendah yaitu pada pengelasan dengan teknik single pass Multilayer di daerah Fusion Line yaitu 42 J.


Abstract

Barata Indonesia Company is a state-owned enterprise (SOE) where operations are carried engaged in the agro industry, oil and gas industry and power generation industries. One of the applications is done by Barata Indonesia Company is developing Storage Tank, which is very spacious tank piled needs in Oil and Gas industry, it is necessary to do the design and fabrication process right. In this study will compare the effects of different strong currents with a single pass welding Chemical engineering and multi-pass multi-layer through testing Radiography Test, Micro etching, Hardness Test and Impact Test. The current strong used are 75A, 90A, and Combination (75-90A), the welding process using SMAW welding machine 2G position and polarity DC ( ), electrodes used all the same E7018 diameter of 2.6 mm. The test results of six specimens were obtained the highest hardness value is the multi-pass multi-layer welding in the area of Weld Metal is 215.62 HVN. The highest average value on impact testing is the single pass welding with multi-layer technique in the area of Weld Metal is 148.5 J and the impact of the lowest value is the single pass welding with multi-layer technique in the Fusion Line is 42 J.


Detil Peneliti

Dosen Pembimbing 1 :Usman Dinata
Dosen Pembimbing 2 : Imam Khoirul Rohmat

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2011


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.