Analisa Pembuatan DAC ( Distance Amplitude Correction ) Pada Sambungan Dissimilar Material Stainless Steel SA 240 Type 304 Dengan Mild Steel SA 36 Terhadap Sensitifitas Hasil Pengujian Ultrasonik

Analysis Of Making DAC ( Distance Amplitude Correction ) on Dissimilar joint Material Stainless Steel SA 240 Type 304 With Mild Steel SA 36 Against Sensitivity Results of Ultrasonic Test

Antonius Wira Nugroho Ponco Sejati (6710040054)


Abstrak

Sambungan dissimilar adalah sambungan berbeda jenis material. Salah satu hal yang penting pada sambungan dissimilar dalam proses inspeksinya NDT ( Nondestructive Test ) tepatnya uji ultrasonik perlunya arah scanning yang tepat dalam menginspeksinya. Beberapa faktor yang dapat mempengaruhi scanning adalah velocity,dan grain size. Untuk mengetahui arah scanning yang tepat dalam inspeksi ini maka dilakukan pengujian. Pada penelitihan ini dilakukan pembuatan DAC ( Distance Amplitude Corection ) untuk mengetahui perbedaan sensitifitas ultrasonik akibat dari velocity dan grain size yang berbeda. Proses scanning ultrasonik pada material dilakukan dua kali, dikarenakan material mempunyai dua velocity yang berbeda, scanning dari arah mild steel dan scanning dari arah stainless steel, terdapat dua sambungan pada pengelasan ini. Sambungan menggunakan elektroda full mild steel dan elektroda full stainless steel sebagai fariasi permasalahan. Dari proses tersebut menghasilkan 4 buah DAC dari sambungan dissimilar dan 2 DAC dari base metal stainless steel dan mild steel. Kemudian hasil dari semua DAC dibandingkan, apabila hasil dari DAC pada pengelasan dan base metal berbeda sensitifitasnya maka perbedaan weld metal mempengaruhi sebuah sensitifitas pengujian ultrasonik. Hasil yang didapat setelah dilakukan pengolahan data yaitu, hasil DAC dari sambungan dissimilar menggunakan dB yang lebih tinggi dari pada DAC yang terbuat dari base metal, hal itu terjadi akibat adanya proses pengelasan yang mengubah grain size sebuah material. Dan hasil dari pemilihan arah scanning yang tepat adalah scanning dari arah stainless steel baik scanning ke arah weld metal full stainless maupun full mild steel.


Abstract

The Dissimilar joint is a joint of different types materials. One of the things that are important of dissimilar joint in process inspection NDT (Non Destructive Test). Actually, the ultrasonic test neet a scanning direction for inspection. some factor can influence direction of scanning is a velocity and grain size. To determine a scanning direction can be proper for this inspection, so will be doing examination. in this examination doing make a DAC ( Distance Amplitude Correction ) for know a different of ultrasonic sensitifity. Scanning process ultrasonic in a material any two scanning, because material have a defferent velocity, so doing scanning from stainless steel direction dan scainning from mild steel direction, any two joint of this welding, any joint using electrode full stainless steel and any joint using elektrode full mild steel this elektrode as a set a problems. the result of this proces heve a four DAC from dissimilar joint and two DAC for base metal stainless steel and base metal mild steel. after that from all result DAC doing comparison. whan a result of dissimilar joint and DAC of base metal any different sensitifity, so the different of weld metal can influence the result from sensitifity ultrasonic test. After this accumulation data getting is, the result of DAC from dissimilar joint using larger dB from DAC of base metal. this problem can happen because consequence welding can change grain size meterial. And a result of the best scanning direction is a scanning direction from Stainless steel, although scainning from weld metal stainless steel and weld metal mild steel


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 : Bachtiar

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.