ANALISIS PENGARUH VARIASI PREHEAT PADA MATERIAL KI GRADE A YANG TELAH TERDEFORMASI PLASTIS DENGAN PEMANASAN TERHADAP NILAI KEKERASAN DAN STRUKTUR MIKRO

ANALYSIS OF THE EFFECT OF PREHEAT VARIATION IN GRADE A OF KI MATERIAL THAT HAVE PLASTIC DEFORMATION WITH HEATING PROCESS ON HARDNESS VALUE AND MICRO STRUCTURE

Deny Angga Setiawan (6710040048)


Abstrak

Pada bagian sisi lambung kapal terdapat pelat baja yang mengalami proses pelengkungan (deformasi plastis). Proses pelengkungan pelat baja biasanya menggunakan proses fairing, material yang terdeformasi dengan fairing ini akan mengalami perubahan struktur mikro dan sifat mekanik karena selama proses terjadi pemanasan dan pendinginan cepat. Dengan kondisi seperti ini maka pelengkungan dengan pemanasan ini akan mengalami perubahan nilai kekerasan dan struktur mikro yang berbeda. Selain itu perubahan nilai kekerasan dan struktur mikro akan mempengaruhi weldability. Penelitian ini membahas tentang pengaruh variasi preheat pada pengelasan material KI Grade A yang telah mengalami deformasi plastis dengan proses fairing. Kondisi pengelasan dalam penelitian ini berupa preheat 60 0C, 90 0C dan 120 0C serta kondisi pengelasan tanpa preheat. Pengujian yang dilakukan dalam penelitian ini adalah uji komposisi kimia, pengujian struktur mikro dan uji kekerasan. Dari pengujian kekerasan yang telah dilakukan pada material KI Grade A, diketahui nilai kekerasan rata- rata tertinggi terjadi pada weld metal pengelasan non preheat sebesar 205,59 HV sedangkan nilai kekerasan terendah terjadi pada base metal pengelasan preheat 120 0C sebesar 135,96 HV. Dari foto mikro yang didapat, struktur yang dominan dari material KI grade A adalah ferritee dan pearlite, dimana temperatur preheat mempengaruhi komposisi ferrite dan pearlite. Semakin tinggi temperatur preheat maka persentase struktur mikro ferritee akan lebih dominan daripada struktur pearlite. Kata kunci: fairing, KI grade A, preheat, struktur mikro, nilai kekerasan


Abstract

At the side of ship there are steel plate that get deformation process (plastic deformation). Deformation process steel plate usually use fairing process. Material that get deformation with fairing process will changes the micro structure and hardness value, because when process go on material get heating and colling rate rapidly. Deformation process with heating will changes the hardness value and micro structure. Beside of that when hardness value an micro structure change would affect in weldability. This research is discuss about effect of preheat variation on grade A of KI material that have experience plastis deformation with fairing process. Welding condition in this research is preheat 60 0C, 90 0C and 120 0C also welding condition without preheat. The testing in this research are chemical composition, micro structure and hardness test. From hardness test that researcher do in grade A of KI material, the result of hardness average its at weld metal non preheat welding with value 205,59 HV, meanwhile lower hardness average its at base metal preheat 120 0C with value 135,96 HV. From microsucture picture, the majority structure from grade A of KI material is ferritee and pearlite in which preheat temperature affected ferritee and pearlite composition. If preheat temperature higher, ferritee microstructure would be dominant than pearlite structure. Kata kunci: fairing, Grade A of KI, preheat, microstructure, hardness value


Detil Peneliti

Dosen Pembimbing 1 :Soeweify
Dosen Pembimbing 2 : Usman Dinata

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.