ANALISIS PENGARUH SUHU INTERPASS TERHADAP KEKERASAN DAN STRUKTUR MIKRO PENGELASAN FILLET JOINT ALUMINIUM PADUAN 5083 DENGAN 6061-T6

ANALYSIS OF THE EFFECT OF INTERPASS TEMPERATURE ON HARDNESS AND MICROSTRUTURE OF FILLET JOINT WELDING ALUMINIUM ALLOY 5083 WITH 6061-T6

Argo Bayu Dahono (6710040045)


Abstrak

Sambungan pengelasan logam tak sejenis antara aluminium paduan 5083 dan 6061-T6 banyak dijumpai pada konstruksi seperti kapal ringan. Sambungan las digunakan karena memiliki keunggulan yang lebih ringan bila dibanding sambungan logam yang lain serta kekuatan las dapat mendekati bahkan melebihi dari kekuatan logam induk. Namun pengelasan dari dua paduan aluminium ini relatif lebih sulit dilakukan karena perbedaan metalugi dan sifat dari dua material ini yang berbeda. Pada tugas akhir ini akan dilakukan analisa pengaruh suhu interpass terhadap nilai kekerasan serta struktur mikro pada pengelasan pipa aluminium paduan 6061-T6 dengan plat aluminium paduan 5083. Pengelasan fillet joint (T joint) aluminium tak sejenis ini menggunakan proses GTAW dengan gas pelindung argon high purity. Pengelasan dilakukan dengan parameter yang sama pada setiap spesimen uji dengan variasi suhu interpass 50?C, 100?C dan 200?C. Hasil Foto mikro menunjukkan perbedaan tampilan Mg2Si2 yang semakin jelas serta butiran yang semakin besar dengan suhu interpass yang semakin tinggi. Hasil pengujian kekerasan diperoleh kecenderungan yang menurun seiring kenaikan suhu interpass pada daerah HAZ aluminium 6061-T6, sedangkan pada daerah yang lain tidak menunjukkan perubahan yang berarti. Kata kunci: aluminium 5083, aluminium 6061-T6, GTAW, suhu interpass, struktur mikro, kekerasan.


Abstract

Different metal welding joints between the aluminium 5083 and 6061-T6 are often found in the construction of such light boat. Welding joints are used because they are lighter when compared to other metal joint and welding strength can approach and even more than the base metal. However, the welding of two combined aluminium is relatively more difficult because of the metallurgy differences and the material characteristics differences. In this final project researcher will analyze the effect of interpass temperature on the hardness value and microstructure in pipe welding aluminium alloy 6061-T6 with plate aluminium alloy 5083. Dissimillar aluminium welding fillet joint (T joint) is using the GTAW process with shielding gas Argon High Purity. Welding is done with the same parameter on each specimen test with variation interpass temperature 50?C, 100?C and 200?C. The photos show the difference in appearance of micro Mg2Si2 increasingly clear and growing grain with higher interpass temperature. Hardness test results obtained trend interpass temperature decreases with the increase in the HAZ of aluminium 6061-T6. Whereas in other areas did not show significant changes. Key Word : aluminium 5083, aluminium 6061-T6, GTAW, interpass temperature, microstructure, hardness


Detil Peneliti

Dosen Pembimbing 1 :Mohammad Thoriq Wahyudi
Dosen Pembimbing 2 :

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.