PENGARUH PENGELASAN OVERLAY PADA STUD FLANGE DENGAN VARIASI HEAT INPUT PADA MATERIAL STAINLESS STEEL 304 TERHADAP LAJU KOROSI

INFLUENCE OF WELDING OVERLAY IN STUD FLANGE WITH HEAT INPUT VARIATIONS ON STAINLESS STEEL 304 MATERIAL AGAINST CORROSION RATE

Wendi Sukma Darmawan (6710040044)


Abstrak

PENGARUH PENGELASAN OVERLAY PADA STUD FLANGE DENGAN VARIASI HEAT INPUT PADA MATERIAL STAINLESS STEEL 304 TERHADAP LAJU KOROSI Nama : Wendi Sukma Darmawan NRP : 6710040044 Jurusan : Teknik Pengelasan Dosen Pembimbing : Ir. Wiwik Dwi Pratiwi, MT ABSTRAK Dengan melakukan penelitian ini diharapkan dapat mengetahui hasil pengelasan overlay stud flange material stainless steel 304 terhadap laju korosi. pada awalnya komponen ini hanya menggunakan stud flange dengan material 304 tanpa diberi perlakuan apapun. Material yang digunakan dalam pengelasan overlay ini adalah stainless steel 304 menggunakan elektroda AWS A5.4 E316L-16 dengan menggunakan proses las busur listrik elektroda terbungkus (SMAW) dengan variasi ampere 60A, 8A, 100A dan 120A serta pembanding adalah material stainless steel 316L tanpa diberi pengelasan overlay. Pengujian korosi dilakukan dengan metode immersion dan elektrokimia sebagai pembanding. Data dari pengujian menunjukkan besarnya laju korosi dalam satuan mmpy. Dari analisa hasil pengujian korosi dengan metode immersion didapatkan bahwa semakin tinggi nilai ampere yang digunakan dalam pengelasan overlay akan menambah nilai heat input dan laju korosi cenderung menurun. Rata-rata nilai laju korosi untuk material tanpa overlay adalah 2.2308 mmpy, ampere 60 dengan heat input 1127.054 J/mm sebesar 2.1767 mmpy, ampere 80 dengan heat input 1386.787 J/mm sebesar 1.6089 mmpy, ampere 100 dengan heat input 1633.595 J/mm sebesar 0.4326 mmpy, dan ampere 120 dengan heat input 1863.443 J/mm sebesar 0.1960 mmpy. Kata kunci : elektrokimia, immersion test, laju korosi, overlay, stainless steel


Abstract

INFLUENCE OF WELDING OVERLAY IN STUD FLANGE WITH HEAT INPUT VARIATIONS ON STAINLESS STEEL 304 MATERIAL AGAINST CORROSION RATE Name : Wendi Sukma Darmawan NRP : 6710040044 Department : Teknik Pengelasan Advisor : Ir. Wiwik Dwi Pratiwi, MT ABSTRACT from this research, researcher hope to konow the result of welding overlay stud flange material stainless steel 304 toward corrosion rate. in the begining this component only use stud flange with 304 material without any treatment. material that use for welding overlay are stainless steel 304, using electorde aws A5.4 E316L-16 with SMAW processs, with variasi ampere 60 A, 8A, 100A dan 120 A also use comparing material that is stainless steel 316L without overlay welding. Corrosion test that researcher do its using immersion methode and electrochemical as comparison. Data from this testing show how much corrosion rate in mmpy. From the result of corrosion test analysis with immersion method, if higher ampere value that use in welding overlay that will increase heat input value and corrosion rate will decrease. corrosion rate value average without overlay is 2.2038 mmpy, ampere 60 with heat input 1127.054 J/mm is 2.1767 mmpy, ampere 80 with heat input 1386.787 J/mm is 1.6089 mmpy, ampere 100 with heat input 1633.595 J/mm is 0.4326 mmpy, and ampere 120 with heat input 1863.443 J/mm is 0.1960 mmpy Keyword : electrochemical, immersion test, corrosion rate, overlay, stainless steel


Detil Peneliti

Dosen Pembimbing 1 :Wiwik Dwi Pratiwi
Dosen Pembimbing 2 :

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.