PENGARUH MULTIPLE REPAIR DENGAN PENGELASAN GAS METAL ARC WELDING TERHADAP SIFAT MEKANIK

MULTIPLE REPAIR EFFECT OF WELDING WITH GAS METAL ARC WELDING ON THE MECHANICAL PROPERTIES

Muchlisin Nur Ikhsan (6710040039)


Abstrak

Kemungkinan terjadinya kesalahan dalam proses pengelasan tidak dapat dihindari dan akan berakibat fatal bagi struktur pengelaan itu sendiri. Hal tersebut diatas dapat terjadi akibat kesalahan nonteknis, seperti kesalahan penggunaan electrode dan kesalahan penerapan filler yang tidak sesuai sehingga terjadi defect. Hal lain yang dapat mengakibatkan terjadinya defect pada hasil lasan adalah pada saat pergantian welder, dalam hal ini sering disebut human error. Untuk mengatasinya diperlukan perlakuan repair, apabila kesalahan dalam proses pengelasan dilakukan berulang kali maka perlu melakukan multiple repair pada weld joint tersebut. Akibat dari multiple repair yang dilakukan akan berpengaruh besar terhadap daerah HAZ dan weldability dari base metal itu sendiri. Pada penelitian ini menggunakan material mild steel yang akan di las dengan mesin las Gas Metal Arc Welding, dimana pada saat pengelasan nanti akan diberikangas pelindung, yaitu 100%CO2.. Setelah itu dilakukan proses repair dengan Arc Gouging dengan kedalaman 50% dan 75% ketebalan sebanyak 3x repair. Hasilnya, material yang mengalami proses repair akan menaikan nilai kekerasan, tapi sebaliknya nilai dari ketangguhan danmaximum stressnya akan menurun. Sedangkan material yang tidak terkena repair, memiliki nilai ketangguhan dan maximum stress yang tinggi dengan nilai kekerasan yang rendah. Kata kunci : repir, kekerasan, ketangguhan, maximum stress.


Abstract

The possibility of errors in the welding process can not be avoided and will be bad for welding structures. This can occur due to non-technical errors, such as errors and faulty implementation of the use of electrode filler that does not conform to occur defect. Another thing that can lead to the occurrence of defects in the weld result was at the turn of the welder, in this case often called human error. To handle the necessary treatment to repair, if the errors in the welding process is repeated multiple times it is necessary to perform the repair at a weld joint. As a result of multiple repair is carried out will greatly affect the HAZ area and weldability of the base metal itself In this study, using a mild steel material to be welded with a welding machine Gas Metal Arc Welding, which at the time of welding will be given a protective gas, which is 100% CO2 . After the repair process is done by Arc Gouging with a depth of 50% and 75% of thickness. As a result, materials that undergo a process of repair will increase the value of hardness, but instead the value of toughness and maximum the stress will decrease. While the material is not subject to repair, has a maximum value of toughness and high stress with low hardness values Keywords: repir, hardness, toughness, maximum stress.


Detil Peneliti

Dosen Pembimbing 1 :Usman Dinata
Dosen Pembimbing 2 : Tri Karyono

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.