ANALISA PENGARUH VARIASI PREHEAT DAN PWHT TERHADAP MECHANICAL PROPERTIES PADA PROSES HARDFACING MATERIAL SS 400

ANALYSIS OF EFFECT OF PRE HEAT AND PWHT VARIATION ON MECHANICAL PROPERTIES OF HARDFACING MATERIAL SS 400

Tri Aditya Kurniawan (6710040038)


Abstrak

Dengan melakukan penelitian ini diharapkan dapat mengetahui hasil pengelasan hardfacing yang akan digunakan dalam pengelasan bucket. Pada awalnya pengelasan hardfacing ini dilakukan tanpa preheat dan PWHT. Material yang digunakan dalam pengelasan hard facing ini adalah SS 400 menggunakan elektroda Nikko Steel HV 600 dengan proses pengelasan SMAW posisi 1G. Pengujian yang dilakukan pada penelitian ini adalah metalography test, hardness test, penetrant test dan wear ressistance. Dari hasil analisa pengujian makro etsa didapatkan semua spesimen mengalami complete fusion pada pengujian hardness dan pengujian wear ressistance didapatkan spesimen dengan variasi preheat 150?C dan PWHT 200?C memiliki nilai kekerasan tertinggi dan laju keausan terendah dikarenakan nilai kekerasan berbanding terbalik dengan nilai laju keausan, pada pengujian penetrant didapatkan linear indication terpendek pada spesimen dengan variasi preheat 150?C dan PWHT 200?C. Kata kunci : hardfacing, metallography test, hardness test, wear resistance test, penetrant test, preheat, PWHT


Abstract

By doing this research be expected can determine the result of hardfacing welding that will be used to weld a bucket. At the begin of this weld hard facing is no using preheat and PWHT. The material used for hardfacing welding is SS 400 using electrodes Nikko Steel HV 600 with SMAW welding process and 1G position. Tests performed is metallography test, hardness test, penetrant test and wear resistance test. From the analysis of the test macro-etching was found all of speciment had complete fusion, in the hardness test and wear ressistance test was found specimen with variation of preheat 150?C and PWHT 200?C had the highest hardness value and lowetst wear rate because hardness value is inversely with value of wear rate, in the penetrant test was found the shortest linear indication in specimen with variation of preheat 150?C and PWHT 200?C. Keywords: hardfacing, metallography test, hardness test, wear resistance test, penetrant test,preheat,PWHT


Detil Peneliti

Dosen Pembimbing 1 :Usman Dinata
Dosen Pembimbing 2 : Bachtiar

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.