ANALISA PERUBAHAN SIFAT MEKANIK DAN STRUKTUR MIKRO MATERIAL PIPA SUPERHEATER 13CrMo44 BOILER YOSHIMINE 1 PG. GEMPOLKREP MUSIM GILING TAHUN 2008-2012

ANALYSIS OF THE MECHANICAL PROPERTIES CHANGES AND MICRO STRUCTURAL MATERIAL OF SUPERHEATAER PIPE 13CrMo44 BOILER YOSHIMIN 1 PG.GEMPOLKREP IN THE SEASON YEAR 2008-2012

Febry Fajar Fanany (6710040032)


Abstrak

ABSTRAK ANALISA PERUBAHAN SIFAT MEKANIK DAN STRUKTUR MIKRO MATERIAL PIPA SUPERHEATER 13CrMo44 BOILER YOSHIMINE 1 PG. GEMPOLKREP MUSIM GILING TAHUN 2008-2012 Nama Mahasiswa : Febry Fajar Fanany NRP : 6710040032 Jurusan : Teknik Bangunan Kapal Dosen pembimbing I : Ir. Soewefy, M.Eng. Dosen pembimbing II : Muhamad Ari, ST., M.Sc. Pada penelitian ini dilakukan analisa secara teknis perubahan sifat mekanik dan struktur mikro yang terjadi pada material 13CrMo44 pemakaian 5 tahun (2008-2012) dengan akumulasi waktu opersional selama 21.600 jam, temperatur operasional 550C-600C, tekanan kerja maksimal 25 kg/cm2 dan temperatur uap rata-rata sebesar 330C. Dengan mengunakan data pembanding material 13CrMo44 baru selama proses pengujian dan analisa. Proses pengujian yang dilakukan dalam penelitian ini adalah pengujian visual, pengujian positive material identification (PMI), pengujian metallografi, pengujian kekerasan, dan pengujian tarik. Penelitian pada material 13CrMo44 pemakaian 5 tahun dibandingkan 13CrMo44 baru membuktikan pada pengujian visual ditemukan terjadinya korosi pada outside surface dan endapan kerak (scale) yang memiliki ketebalan rata-rata 2,2 mm pada inside diameter pipa. Pada pengujian PMI terjadi kenaikan kandungan karbon sebesar 0,03% dan penurunan Cr sebesar 0,66%. Pada pengujian metallografi terjadi pembesaran butiran pearlite dan terbentuknya endapan karbida Mo2C dan Cr7C3 pada butiran ferrite dan pada batas butir. Pada pengujian tarik terjadi kenaikan kuat tarik rata-rata sebesar 40,58 Mpa. Dan pada pengujian kekerasan terjadi kenaikan nilai kekerasan pada outside surface rata-rata sebesar 22,7 HV dan pada inside surface rata-rata sebesar 13,1 HV. Terjadi kenaikan kuat tarik setiap tahunya sebesar 115,86 Mpa. Dan dapat disimpulkan material 13CrMo44 pemakaian 5 tahun masih dapat digunakan kembali dalam proses opersional 1 tahun kedapan karena masih dalam batas kuat tarik yang diijinkan standart DIN 17175. Kata kunci : Material 13CrMo44, Pipa Superheater, Pengujian Visual, PMI, Pengujian Metallografi, Pengujian Tarik, Pengujian Kekerasan.


Abstract

ABSTRACT ANALYSIS OF THE CHANGES OF MECHANICAL PROPERTIES AND MICRO STRUCTURAL MATERIAL OF SUPERHEATAER PIPE 13CrMo44 BOILER YOSHIMIN 1 PG.GEMPOLKREP IN THE SEASON YEAR 2008-2012 Nama : Febry Fajar Fanany NRP : 6710040032 Departement : Ship Building Engineering Final Project Adviser I : Ir. Soewefy, M.Eng. Final Project Adviser II : Muhamad Ari, ST., M.Sc. In the reaserch, the analysis was done technically on the mechanical properties and micro structural change that occurred in the material of 13CrMo44 which has been used for 5 years (2008-2012) with accumulation of time temperature over 21.600 hours, operational temperature by an average 550C ? 600C, maximum working pressure 25 kg/cm2 and steam temperature by an average 330C. By using comparative data of new material 13CrMo44 during the process of the testing and analysis. The testing process carried out in this reaserch was a visual test, positive material identification test (PMI), metallography test, tensile test and hardness test. The reaserch on material 13CrMo44 which has been used for years finally proved that in visual testing, corrosion was found on the outside surface and sediment scale which had average thickness of 2,2 mm in the inside diameter pipe. At the PMI testing there was an increase carbon content 0,03% and decrease chromium content 0,66%. In metallography testing there was enlargemen of pearlite grain and formation carbide Cr7C3 and Mo2C in the ferrite grains and at grain boundaries. In tensile test, there was an increase of tensile strength average 40,58 Mpa. And in the hardness testing there was an increase of hardness value on the outside surface average 22,7 HV and on the inside surface average 13,1 HV and increase tensile strength every years average 115,86 Mpa. And the conclusion material of 13CrMo44 which has been used for 5 years can operational 1 years again because tensile strength not exceed range standart DIN 17175. Keyword: Material 13CrMo44, Superheater Pipe, PMI, Metallography test, Tensile test, Hardness test


Detil Peneliti

Dosen Pembimbing 1 :Soeweify
Dosen Pembimbing 2 : Muhamad Ari

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.