ANALISA PENGARUH DEFORMASI PLASTIS TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO PADA LOW ALLOY STEEL MENGGUNAKAN METODE PENGELASAN SMAW

ANALYSIS ON THE EFFECT OF PLASTIS DEFORMATION TOWARD MECHANICS CHARACTERISTIC AND MICRO STRUCTURE ON LOW ALLOY STEEL BY USING SMAW WELDING PROCESS

Rezatri Kimia Dwi Rizki (6710040031)


Abstrak

Pada umumnya cukup banyak perlakuan yang diberikan terhadap material sebelum dilakukan pengelasan untuk mendapatkan bentuk dan ukuran yang sesuai dengan bagian yang diinginkan. Salah satunya dengan proses pelengkungan. Akibat perlakuan tersebut material akan mengalami perubahan bentuk dari struktur mikro dan sifat mekaniknya serta adanya kemungkinan terjadinya crack karena mengalami strain hardening. Material yang digunakan adalah jenis Low Alloy Steel. Setelah material mengalami deformasi plastis selanjutnya material akan dilakukan proses pengelasan SMAW. Deformasi plastis terhadap material dilakukan dengan 3 variasi besar radius pembentukan yaitu R 250 mm, R 350 mm dan R 450 mm. Uji visual, uji metalografi dan uji kekerasan akan dibutuhkan untuk mengatahui seberapa besar pengaruh yang didapatkan material. Hasil dari penelitian menunjukkan material mengalami perbedaan pada bentuk struktur mikro dan nilai kekerasan. Struktur mikro material R 250 mm lebih terlihat kasar disbanding dengan R 350 mm dan R 450 mm. Serta terjadi nilai kekerasan terendah pada material R 250 mm sebesar 196.5 HV di daerah weld metal. Pada daerah lain perbedaan nilai kekerasannya tidak terlalu signifikan. Kata kunci : kekerasan, struktur mikro, crack


Abstract

Generally has many treatment for the material before welding to get some shape and size appropriate with the section. One of which use the rolling process. Consequence from this treatment is can change shape of micro structure and mechanics characteristic. Maybe material can experience for crack because strain hardening. The material used is Low Alloy Steel. After material have experience of deformation plastis, material will on welding process with of SMAW method. The plastis deformation on the material with 3 variation radius plasticity, R 250 mm, R 350 mm and R 450 mm. Visual test, metallography test and hardness test will need for know as much as influence for the material. The final result of the examination show the material experience diverivication at shape of micro structure and value of hardness. Material with R 250 mm have a coarse micro structure more than material with R 350 mm and R 450 mm. Material also have change value of hardness and have a lower value of hardness at weld metal section in material R 250 mm, the result is 196.5 HV. At the other section change value of hardness can?t excessively. Key word : hardness, micro structure, crack


Detil Peneliti

Dosen Pembimbing 1 :Bachtiar
Dosen Pembimbing 2 : Usman Dinata

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.