PENGARUH DISTRIBUSI PANAS PENGELASAN BERDASARKAN VARIASI DESAIN SAMBUNGAN LAS TERHADAP NILAI KEKERASAN DAN STRUKTUR MIKRO LOGAM BIMETAL AL/FE SEBAGAI ALTERNATIF DISSIMILAR METAL WELDING

THE INFLUENCE OF WELDING HEAT DISTRIBUTION BY VARIATION WELD JOINT DESIGN ON HARDNESS VALUE AND MICROSTRUCTURE OF AL/FE TRANSITION JOINT METAL AS AN ALTERNATIVE DISSIMILAR METAL WELDING

Wahyu Lailil Fais (6710040027)


Abstrak

Hadirnya logam bimetal Al/Fe sebagai alternatif baru pengelasan dissimilar metal alumunium dan baja sangat membantu dalam produktivitas di industri galangan kapal, khususnya penyambungan bangunan atas dengan bangunan bawah kapal. Dimana dalam penyambungan pengelasan pada logam terdapat berbagai macam desain sambungan. Pada penelitian ini dilakukan 5 variabel desain sambungan yaitu fillet dan single bevel dimana pada lebar logam bimetal yang berbeda lalu dilakukan pengujian kekerasan dan pengamatan struktur mikro. Hasil dari penelitian ini menunjukkan bahwa struktur mikro dan nilai kekerasan pada logam bimetal dengan nilai yang optimal pada variasi desain sambungan fillet joint logam bimetal lebar 20mm. Penelitian ini nantinya akan bermanfaat sebagai refrensi bagi industri maupun fabrikasi terutama bagi PT. PAL Indonesia. Kata kunci : logam bimetal, struktur mikro, kekerasan, desain sambungan, perbedaan lebar bimetal,


Abstract

The presence of bimetallic Al/Fe transition joint as an new alternative dissimilar metal welding aluminum and steel are very helpful in productivity in the shipbuilding industry, in particular to connecting above and bottom of building construction in the shipbuilding industry. Which in welding, there are various weld join designs of a metal connection. Single bevel, fillet joint and the different width of bimetal are to be the variables in this study. To observe the influence of variables, microhardness testing and metalography are performed in this study.The results of this study indicate that the microstructure and hardness in bimetal with optimum value in the fillet joint with width 20 mm of bimetal. And then, will this study will be useful as references for the industry as well as fabrication, especially for Indonesian PT.PAL Indonesia Keywords : bimetallic Al/Fe transition joint, microstructure, hardness, weld join design, different width of bimetal


Detil Peneliti

Dosen Pembimbing 1 :Moh. Miftachul Munir
Dosen Pembimbing 2 :

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.