PENGARUH SOLUTION TREATMENT PADA HASIL PENGELASAN OVER HEAT INPUT PADA MATERIAL SA240 TYPE 304 TERHADAP KEKERASAN DAN KEPEKAAN INTERGRANULAR CORROSION ATTACK

THE IMPACT OF SOLUTION TREATMENT TO THE OVER HEAT INPUT WELDING RESULT ON MATERIAL SA 240 TYPE 304 TO HARDNESS AND SUSCEPTIBILITY TO INTERGRANULAR CORROSION

M. Afif Syaichoni (6710040025)


Abstrak

ABSTRAK ? PENGARUH SOLUTION TREATMENT PADA HASIL PENGELASAN OVER HEAT INPUT PADA MATERIAL SA240 TYPE 304 TERHADAP KEKERASAN DAN KEPEKAAN INTERGRANULAR CORROSION ATTACK ? Oleh : M Afif Syaichoni NRP : 6710040025 Dalam dunia Industri, Manufaktur maupun fabrikasi terutama dalam proyek pembangunan suatu perusahaan, Salah satunya dalam proyek pembangunan pabrik PT. PETRO JORDAN ABADI yang terdapat proses fabrikasi item converter dengan menggunakan material austenitic stainless steel (SA 240 Type 304), dan filler metal yang digunakan yaitu E308 / 308H-16 dengan proses pengelasan SMAW. Namun dalam penggunaan aplikasinya terdapat korosi intergranular yang dikarenakan karbida krom yang terjadi akibat hasil pengelasan over heat input, untuk memperbaiki karbida krom yang telah terjadi maka diperlukan perlakuan solution treatment dengan tujuan untuk melarutkan karbida krom yang telah terjadi.. Pada penelitian ini dilakukan pada 3 variabel proses solution treatment antara lain solution treatment temperature 850?C, 900?C, dan 950?C yang diaplikasikan pada hasil pengelasan. kemudian dilakukan pengujian kekerasan vickers dan pengujian korosi intergranular berdasarkan standart ASTM A 262 practice B. Hasil dari penelitian ini menjelaskan bahwa solution treatment temperature 950?C mengakibatkan terjadinya penurunan kekerasan dan kepekaan terhadap serangan korosi intergranular. Penelitian ini nantinya akan bermanfaat sebagai refrensi bagi industri maupun fabrikasi terutama bagi PT. PETRO JORDAN ABADI. Kata kunci : Material SA 240 Type 304, Solution treatment, pengelasan over heat input, korosi intergranular.


Abstract

ABSTRACT ?SOLUTION TREATMENT IMPACT AT OVER HEAT INPUT WELDMENT ON SA240 TYPE 304 TO HARDNESS AND SUSCEPTIBILITY TO INTERGRANULAR CORROSION ATTACK ? By : M Afif Syaichoni NRP : 6710040025 On the Industrial, Manufacturing and on site fabrication especially on the company building project, such as plant project on PT. PETRO JORDAN ABADI which is contained fabrication process for converter items that used austenitic stainless steel (SA 240 Type 304) materials, and the filler metal used is E308 / 308H-16 with the SMAW welding process. However, on its application there are some intergranular corrosion caused the over heat input on welding result so there are chromium carbide inside it. To repair the chromium carbide that has been occurs, the solution treatment becomes the best solution to dissolve the chromium carbide. This research conducted to 3 solution treatment variables process that is solution treatment for 850 ? C, 900 ? C and 950 ? C that applied to the weldment. Then do such a hardnes vickers test and intergranular corrosion test based on ASTM A 262 practice B. The result of this expertment will be explain that the solution treatment for 950?C caused decreasing of hardness and susceptibility to intergranular corrosion attack. This experiment will be the beneficial references for the industrial and fabrication, especially for PT. PETRO JORDAN ABADI. Keywords :Material SA 240 Type 304, Solution treatment, over-heat input welding, intergranular corrosion.


Detil Peneliti

Dosen Pembimbing 1 :Moh. Miftachul Munir
Dosen Pembimbing 2 : Wiwik Dwi Pratiwi

Program Studi : D4 - TEKNIK PENGELASAN
Angkatan : 2010


Untuk mendapatkan versi full dari dokumen penelitian ini, Anda dapat melihat koleksi Buku Tugas Akhir di Perpustakaan Politeknik Perkapalan Negeri Surabaya pada jam kerja. Atau Anda dapat menghubungi penulis secara personal.